Marine Adhesive/Sealant Fast Cure 5200 06520 05220 Technical Data February, 2012 Product Description 3M Marine Adhesive/Sealant Fast Cure 5200 is a fast curing, one-part polyurethane that chemically reacts with moisture to deliver strong, flexible bonds with excellent adhesion to wood and fiberglass. Forms watertight, weather-resistant seals on joints and boat hardware, above and below the waterline. In addition, its flexibility allows for dissipation of stress caused by shock, vibration, swelling or shrinking. 3M Marine Adhesive/Sealant Fast Cure 5200 06520 10 fl. oz. cartridge (295 ml) - White Product Construction 3M Marine Adhesive/Sealant Fast Cure 5200 05220 3 fl. oz. tube (90 ml) - White Features Tough/flexible polyurethane polymer. Non-shrinking. One-part moisture cure. Non-sagging formula. Fast cure formula. Typical Physical Note: The following technical information and data should be considered representative or typical only and should not be used for specification purposes. Properties Container: 10 fl. oz. (295 ml) cartridge 3 fl oz. (90 ml) tube Base: Polyurethane Density lbs/Gallon (Approx.): 11.0 lbs/gallon Color: White Solids Content (Approx.) 97% Consistency: Medium paste Service Temperature: -40F to 190F (-40C to 88C) Shore A Hardness (cured): 60 Specific Gravity: 1.21 Coverage (10 oz.): 1/8 inch (0.3175 cm) bead = 120 lineal feet (36.6 m) 3M Marine Adhesive/Sealant Fast Cure 5200 06520 05220 Note: The following technical information and data should be considered representative Performance Properties or typical only and should not be used for specification purposes. Tensile and Elongation Test: A 1/8 inch (0.3175 cm) dumbbell specimen with a 1/8 inch (0.3175 cm) square cross section was tested at 2.0 inches/minute (5.08 cm/minute). Relative Tensile Strength Elongation 2 Humidity Temperature psi (kg/cm ) (%) 50% 70F (21C) 1000 (70.3) 874 Overlap Shear Strength: One inch (2.54 cm) overlap specimens (0.093 inch 0.2362 cm thickness). Samples cured at 70F (21C), 50% relative humidity. 2 Substrate psi kg/cm Wood(s): Teak 335 25.0 Pine 543 38.2 Oak 518 36.4 Maple 597 42.0 Fir 600 42.2 Mahogany 407 28.6 Metal(s): Steel 316 22.2 Stainless Steel 197 13.8 Aluminum 203 14.3 Brass 184 12.9 Bronze 176 12.4 Copper 182 12.8 Lead 160 11.2 Zinc (Galvanized) 269 18.9 Plastics/Polymers: Fiberglass 269 18.9 Gelcoat 600 42.2 Polycarbonate 409 28.7 Acrylic 149 10.5 Nylon 140 9.8 ABS 262 18.4 Polypropylene 66 4.6 Polyethylene 0 0 - 2 -