5589H 3M

Technical Data November 2013 3M Thermally Conductive Acrylic Interface Pad 5589H Product Description 3M Thermally Conductive Acrylic Interface Pad 5589H is a soft acrylic based pad designed to provide a preferential heat transfer path away from heat generating components. Because of its softness, 3M Interface Pad 5589H can decrease the load to integrated circuit chips during compression, and provides good tack to many surfaces. These properties lead to a high performance non-silicone based thermal pad. Good softness and conformability to non-flat surfaces. Excellent compressive stress relaxation. High thermal conductivity. UL94 V-O certified (File No. E176845). Good surface tack leads to low thermal resistance at surface. Non-silicone acrylic elastomer. Good dielectric performance. Excellent durability for long term thermal conductivity and electric insulation stability. Product Construction Film liner (Roll type: Film on firm layer) Thermally conductive firm acrylic elastomer (very low tack) surface Thermally conductive soft acrylic elastomer (low tack) core 3 3M Thermally Conductive Acrylic Interface Pad 5589H Typical Physical Properties and Performance Characteristics Note: The following technical information and data should be considered representative or typical only and should not be used for specification purposes. Property Method Value 3M Thermally Conductive Acrylic Interface Pad 5589H Color Light grey / White Thickness (mm)** 5 mm dia. dial gauge 1.0 / 1.5 Thermal Conductivity (W/m-K) 3M method 2.0 Flammability UL94 V-O 3 Density (g/cm , 25C) JIS K6249 1.9 Hardness Asker C 16 (data for soft layer) Shore 00* 50 12 Volume Resistivity ( -cm) JIS K6249 3.4 x 10 Dielectric Strength (kV/mm) JIS K6249 21 Note: *Shore 00 test method results are based on a 6mm thick sample. Results will vary with sample thickness. Sample tested to soft layer side of the pad. **Tolerances of 1 mm and 1.5 mm = +/-10%, 0.5 mm +/- 0.1 mm. 3M Thermally Conductive Acrylic Interface Pad 5589H Heat Stability Duration (hrs) Initial 500 1000 2000 Thermal Conductivity (W/m-K) 2.0 2.0 2.0 2.0 Hardness (Asker C) 16 17 16 17 Appearance No effect No effect No effect Aged at 110C in high temperature chamber. 3M Thermally Conductive Acrylic Interface Pad 5589H UL Rating In Service Temperature Resistance Short Term (Hours-Days) 110-130C UL94VO Long Term (Weeks-Months) 90-100C (2)