3 High Performance Double Coated Tapes with Adhesive 375 9086 9087 9088 9088FL Technical Data March, 2007 Product 3M Double Coated Tapes with 3M Adhesive 375 provides a high level of adhesive peel Description and shear performance. The adhesive system used on these products provides good adhesion to both high and low surface energy substrates. The excellent initial tack ensures that a bond of good integrity is achieved soon after application. Total Tape Construction Thickness Tape Liner Color, Liner Tape Product Adhesive w/o Liner Color Carrier Type, Print Caliper Color 3M Double Modified 7.5 mils Translucent Tissue White Paper 3.0 mils Translucent Coated Tape Acrylic (0.19 mm) (Glassine) (0.07 mm) 9086 with Black 3M Logo 3M Double Modified 10.2 mils White PVC White Paper 3.0 mils White Coated Tape Acrylic (0.26 mm) 1.5 mils (Glassine) (0.07 mm) 9087 with Green 3M Logo 3M Double Modified 8.3 mils Clear Polyester White Paper 3.0 mils Clear Coated Tape Acrylic (0.21 mm) 0.5 mils (Glassine) (0.07 mm) 9088 with Red 3M Logo 3M Double Modified 8.3 mils Clear Polyester Red 3.1 mils Clear Coated Tape Acrylic (0.21 mm) 0.5 mils Polypropylene (0.08 mm) 9088FL Film, No Print 3M High Performance Double Coated Tapes with Adhesive 375 9086 9087 9088 9088FL Note: The following technical information and data should be considered representative Typical Physical Properties or typical only and should not be used for specification purposes. and Performance Characteristics 3M Double Coated Tapes Typical 9086 9087 9088 9088FL Adhesion Oz/in (N/10 mm) Oz/in (N/10 mm) Oz/in (N/10 mm) Oz/in (N/10 mm) 146 142 137 137 Stainless Steel (16) (16) (15) (15) 162 146 155 155 Polycarbonate (18) (16) (17) (17) 180 Degree Peel 146 164 128 128 Glass ASTM D3330 (16) (18) (14) (14) Modified, 2-mil Aluminum Backing 137 146 119 119 ABS (Faceside Adhesion) (15) (16) (13) (13) 68 82 64 64 HDPE (7) (9) (7) (7) High Pressure 119 119 101 101 Laminate (13) (13) (11) (11) Typical Sheer Temperature Minutes to Minutes to Minutes to Minutes to Performance Weight Failure Failure Failure Failure 72F (22C) 10,000 10,000 10,000 10,000 1000g ASTM D3654 158F (70C) 2 modified (1-inch 10,000 10,000 10,000 10,000 500g sample size) 200F (93C) 10,000 10,000 500g Continuous 185F 158F 200F 200F (Days/Weeks) (85C) (70C) (93C) (93C) Temperature Performance Short Term 248F 185F 300F 300F (Hours/Minutes) (120C) (85C) (150C) (150C) Solvent Resistance Good Good Good Good UV Resistance Excellent Excellent Excellent Excellent (1) Plasticizer Resistance Good Good Good Good (1) All products show good resistance to plasticizer migration. However due to the wide range of plasticizers available we strongly suggest that an evaluation is conducted prior to use to ensure compatibility. Sampling substrates with tape applied for 10 days at 158F (70C) will usually accelerate any potential problems. Plasticizers are typically found in materials such as polyvinyl chloride and some rubber products. POP Displays Plastic Extrusions Application Ideas Metal Fabrication Blister Packs and Packaging Sports Equipment Badge and Nameplates Indoor/Outdoor Signs Fabric and Leather Stitching Blind Manufacturers Print Finishing Furniture Trim Splicing - 2 -