VHB 9469PC Adhesive Transfer Tape Product Data Sheet Updated : November 2001 Supersedes : February 1999 A-10 is a very firm acrylic pressure-sensitive system. It features very high shear holding Product Description power. Bond strength increases substantially with natural ageing. Acrylic Physical Properties Adhesive Type 3M ref : A-10 Not for specification purposes Thickness (ASTM D-3652) Tape 0.13 mm 5 Thou Liner 0.10 mm Total 0.23 mm Poly Coated Tan Paper. Printed Green 3M VHB Release Liner Clear Tape Colour 12 months from date of despatch by 3M when stored in the Shelf Life original carton at 21C (70F) & 50 % Relative Humidity 13.1 N/10mm Please see Peel Adhesion Performance Peel Adhesion to Steel 180 peel room temp, 72 hr dwell, Continued on next page. Characteristics jaw speed 300mm/min ASTM D-3330 Not for specification purposes Static Shear Strength Minutes to failure weight held for 10,000 mins to stainless steel 1000g 20C 10,000+ with sq in (3.23 sq cm) overlap 1000g 65C 10,000+ 1000g 95C 10,000+ 1000g 120C 10,000+ 500g 150C 10,000+ 500g 175C 7,500+ Temperature Performance 260C Minutes/Hours 150C Days/Weeks When properly laminated between two impervious Solvent Resistance materials, adhesive will resist mild acids and alkalies, most oils, grease, gasoline, kerosene, JP-4 fuel, hydraulic fluids and other typical aromatic and aliphatic hydrocarbon and ketone solvents. 2 Date : November 2001 9469PC VHB Transfer Tape Excellent. Performance UV Light Resistance Characteristics (Cont..) Not for specification purposes When properly laminated between two impervious Water Resistance materials and submitted to 100 hour immersion in water at 20C the adhesive bond is not affected. Environmental Peel adhesion tests on tapes applied to glass, stainless steel, and aluminium and subjected to 1000 hours Resistance Weather - ometer exposure showed no decrease in bond strength and no degradation of the adhesive. Adhesive laminated between glass and clear polyester and exposed to Florida sunshine for 1 year showed no degradation of the adhesive. 6 >1 x 10 Insulation Resistance Peel Adhesion (Cont...) Stainless Steel 13.1 N/10mm 180 peel room temp, 72 hr dwell, Aluminium 13.1 N/10mm jaw speed 300mm/min ASTM D-3330 Rigid Vinyl 9.8 N/10mm ABS 7.7 N/10mm Polycarbonate 9.8 N/10mm Glass 9.8 N/10mm Acrylic 9.8 N/10mm Epoxy 9.8 N/10mm Thermal Conductivity Dielectric Strength A-10 acrylic adhesive is Additional Product (Volts/25m) designed for applications Information Watt/cm C 3,500 Volts requiring high peel and shear strength. 0.0016 Performance data on various tests are shown above.