: July 2000
: June 1995
2.0 thou (50 micron) #200MP Hi-Performance Acrylic
0.5 thou (12.5 micron) Transparent Polyester
2.0 thou (50 micron) #200MP Hi-Performance Acrylic
Liner 4.0 thou (100 micron) 94g/m 58# Polycoated Kraft
4.1
Shelf Life 24 months from date of manufacture when stored in
cartons at 70F at 50% relative humidity.
A thin polyester carrier provides improved handling with ease of die cutting and
laminating compared to free film adhesives.
chemical resistance and withstands tough application environments.
Moisture - stable liner provides easy removal and improves processing of parts.
Ideal for graphic overlays, nameplates, appliqus and decorative trim.
Excellent for foam lamination.
Temperature Range
40C (-40F) to 250F (121C) for days or weeks and to
300F (149C) for minutes or hours.
Chemical Resistance
adhesive resists mild acids and alkalis, oil, gasoline,
kerosene, JP-4 fuel and many other solvents. It is not
recommended for
total immersion.
Humidity Resistance
relative humidity at 100F (38C).
No adverse effect on the bond after exposure to100%
(Not for specification purposes)
steel test surface.
faceplate materials to a stainless
the adhesion of impervious
Excellent solvent resistance when properly applied. The
Properties defined are based on
Performance
#200MP adhesive has a temperature range of - Properties and
Applications
#200MP Hi - Performance acrylic adhesive provides exceptional temperature and
Features:
Adhesive
Carrier
Not for specification purposes
Adhesive Physical Properties
Supersedes
Updated
Product Data Sheet
Double Coated Laminating Adhesive 9495MP
Scotch2
Date :
Double Coated Laminating
to air or ultraviolet light.
function of time and temperature.
Initial Adhesion - Dynamic Peel 180 (ASTM D-3330, PSTC3)
Die Cutting:
Good die-cuttability. Lubricate dies with vanishing oil or similar low residue lubricants
for improved processing.
Roll Laminating:
substrate contact a nip area only.
Special Considerations Bond strength is
Firm application pressure develops better adhesive contact and thus improves bond
strength.
To obtain adhesion, the bonding surfaces must be clean, dry, and smooth. Typical
cleaning solvents are isopropyl alcohol or heptane. Consult solvent manufacturers
Material Safety Data Sheet for proper handling and storage instructions.
Ideal tape application temperature range is 21C to 38C (70F to 100F) Initial tape
application to surfaces at temperatures below 10C (50F) is not recommended
applied, low temperature holding is satisfactory.
3M and Scotch are trademark s of the 3M Company.
Tapes & Adhesives Group
3M Ireland
3M House, PO Box 1, 3M House, Adelphi Centre,
Market Place, Tel 0870 60 800 50 Upper Georges Street, Tel (01) 280 3555
Bracknell, Berkshire, Fax 0870 60 700 99 Fax (01) 280 3509
Ireland RG12 1JU
Dun Laoghaire, Co. Dublin,
Customer Service : Product Information : 3M United Kingdom PLC
3M United Kingdom PLC 2000
recommendations.
This is because 3M cannot accept any responsibility or liability direct or consequential for loss or damage caused as a result of our
determine their suitability for your applications.
Our recommendations on the use of our products are based on tests believed to be reliable but we would ask that you conduct your own tests to
Values presented have been determined by standard test methods and are average values not to be used for specification purposes.
because the adhesive becomes too firm to readily adhere. However, once properly
upon the amount of adhesive-to-surface contact developed. dependent
Use rubber over steel roll set up with moderate application pressure. Make adhesive to
Processing
4.0 N/10mm Stainless Steel
Not for specification purposes
Adhesion Properties
The bond strength of #200MP adhesive increases as a
Bond Build Up
Performance Contd
Properties and
Adhesive is resistant to oxidation and ozone when exposed U.V. Resistance
Adhesive 9495MP
July 2000