DP-100+ CLEAR 1.7 FL OZ 3M

3 TM Scotch-Weld Epoxy Adhesives DP-100 Clear DP-100 NS Translucent Technical Data December, 2009 Product Description 3M Scotch-Weld Epoxy Adhesives DP-100 and DP-100NS are two-part adhesives offering fast cure and machinability. Available in larger containers like 3M Scotch-Weld Epoxy Adhesives 100 B/A or 100 NS B/A. Features Easy mixing High Flow (Scotch-Weld DP-100 Clear) Non-Sag (Scotch-Weld DP-100 NS Translucent) Fast Cure Scotch-Weld DP-100 meets UL 94 HB Note: The following technical information and data should be considered representative Typical Uncured or typical only and should not be used for specification purposes. Physical Properties Product 3M Scotch-Weld Epoxy Adhesive DP-100 Clear DP-100 NS Translucent 1 Viscosity Base 8,000-15,000 cps 90,000-150,000 cps 73F (23C) Accelerator 9,000-16,000 cps 50,000-85,000 cps Base Resin Epoxy Epoxy 4 4 Color Clear/Lt. Amber Translucent Net Weight Base 9.5-9.9 9.6-10.0 (Lbs./Gallon) Accelerator 9.2-9.6 9.2-9.6 Mix Ratio (B:A) Volume 1 : 1 1: 1 Weight 1 : 0.98 1 : 0.96 2 3 Worklife 10 g mixed 5 minutes 5 minutes (Gel time ) 73F (23C) 1. Viscosity determined using 3M test method C-1d. Procedure involves Brookfield RVF, 6 spindle, 20 rpm and 80F (27F). (100 Clear) and 6 spindle, 4 rpm and 80F (27F) (100 NS). Measurement taken after 1 minute. 2. Worklife determined using 3M test method C-548. Procedure involves periodically measuring a 10 gram mixed mass for spreading and wetting properties. This time approximates the usable worklife in an EPX applicator nozzle. 3. Gel time determined using 3M test method C-554. Procedure involves periodically checking a 10 gram mixed mass for flowing properties. 4. Color may vary from nearly white to yellow/amber. Adhesive performance is not affected by color variation. 3M Scotch-Weld Epoxy Adhesives DP-100 Clear DP-100 NS Translucent Note: The following technical information and data should be considered representative Typical Cured or typical only and should not be used for specification purposes. Properties Product 3M Scotch-Weld Epoxy Adhesive DP-100 Clear DP-100 NS Translucent Physical: 11 11 Color Translucent Translucent Shore D Hardness 80-85 80-85 (ASTM D 2240) 5 Time to Handling Strength 15-20 min. 23C (73F) 15-20 min. 23C (73F) 6 Cure Time 24-48 hours 23C (73F) 24-48 hours 23C (73F) Thermal: Wt. loss by Thermal 5% 307C (585F) 7 Gravimetric Analysis 8 Glass Transition Temp 33C (91F) 34C (86F) 9 -6 -6 Coefficient of Thermal 60 x 10 (-40C to +20C) 29 x 10 (-50C to +30C) Expansion (in./in./C) (-38F to +68F) (-56F to +86F) -6 -6 209 x 10 (60C to 120C) 149 x 10 (50C to 110C) (+140F to +248F) (+122F to +230F) 10 Thermal Conductivity 0.107 46C (115F) 0.106 45C (113F) (btu-ft./sq. ft.-hr. F) Electrical: Dielectric Strength 860 volts/mil 1100 volts/mil (ASTM D 149) 12 14 Volume Resistivity 3.5 x 10 ohm-cm 2.2 x 10 ohm-cm (ASTM D 257) 5. Handling strength determined per 3M test method C-3179. Time to handling strength is the time required to achieve 50 psi OLS strength to aluminum. 6. The cure time is defined as the time required for the adhesive to achieve a minimum of 80% of its ultimate OLS on aluminum. 7. Weight loss by Thermal Gravimetric Analysis reported as that temperature at which 5% weight loss occurs by TGA in air at 5C (41F) rise per minute per ASTM 1131-86 Test Procedures. 8. Glass transition temperature (Tg) determined using Perkin Elmer (DSC) Analyzer with a heating rate of 20C (68F) per minute. Second heat values given. 9. Coefficient of thermal expansion determined using DuPont (TMA) using a heating rate of 10C (50F) per minute. Second heat values given. 10. Thermal conductivity determined using ASTM C177 and C-matic Instrument with 2 in. diameter samples. 11. Color may vary from nearly white to yellow/amber. Adhesive performance is not affected by color variation. - 2 -