KVF101L104M31NLT00 Chemi-Con

MULTILAYER CERAMIC CHIP CAPACITORS High RoHS2RoHS AEC- Compliant temperature Compliant Q200 Series KVF 150 Temperature cycle : 1000 cycles FEATURES 1. Temperature range : -55 to +150 2. Temperature characteristics : X8L 3. Exellent noise absorption. 4. Automotive grade (AEC-Q200) APPLICATIONS 1. Noise filter for automotive equipment (ECU etc.) 2. Equipment used in a high temperature environment CONSTRUCTION Ceramic Dielectric Termination (Tin Plating) Internal Electrode RATINGS 1. Category Temperature Range -55+150 2. Rated Voltage Range 25, 50, 100 Vdc 3. Rated Capacitance Range 0.03315F 4. Rated Capacitance Tolerance M(20) 5. Temperature Characteristics X8L 6. Rated Ripple Current See No.5 on the following table SPECIFICATIONS No. Items Specification Test Condition 1 Withstand Voltage No abnormality. 250% of rated voltage shall be applied for 5 seconds. 2 Insulation Resistance 100/CR(M) or 4000(M) Rated voltage shall be applied for 605 seconds at temperature 252. whichever is less. 3 Rated Capacitance Within specified tolerance. CR 10F CR>10F Temperature 252 4 Dissipation Factor 5.0% maximum. Frequency 10.1kHz 12012Hz Voltage 10.2Vrms 0.50.2Vrms 10kHz1MHz (sine curve) 5 Rated Ripple Current Ripple voltage Vp shall be less than Size code 31 32 43 55 the rated voltage. Arms 0.3 0.5 1.0 2.0 The surface temperature MLCC must not exceed the maximum category temperature when the ripple current is applied. As customer requirement, Chemi-Con has submits the test results according to AEC-Q200 for Multilayer ceramic capacitors. Please contact us for more information. Product specifications in this catalog are subject to change without notice.Request our product specifications before purchase and/or use. Please use our products based on the information contained in this catalog and product specifications. 19 CAT. No. E1002Z Ver.2MULTILAYER CERAMIC CHIP CAPACITORS KVFSeries SPECIFICATIONS No. Items Specification Test Condition Appearance : No abnormality. Temperature Max. category temperature3 48 High Temperature C/C : 20% Time1000 hours 0 6 Exposure D.F. : 10% maximum (Storage) I.R. 50/CR(M) or 1000(M) whichever is less. Appearance : No visible damage. Step Temperature () (min.) C/C : 15% 1 Min.Category temperature3 303 D.F. : To meet the initial specification. 2 Room temperature 3 max. I.R. : To meet the initial specification. 7 Temperature Cycle 3 Max. Category temperature3 303 4 Room temperature 3 max. (Epoxy resin PCB t=1.6mm) For 1000 cycles Appearance : No abnormality. Temperature 853 C/C : 20% Humidity 80 85%RH 8 Biased Humidity D.F. : 10% maximum Voltage Rated voltage 48 I.R. : 25/CR(M) or 1000(M) Time1000 hours 0 whichever is less. Appearance : No abnormality. Temperature Max. category temperature3 C/C : 20% Voltage Rated voltage 48 9 Operational Life D.F. : 10% maximum Time1000 hours 0 I.R. : 50/CR(M) or 1000(M) whichever is less. Appearance : No abnormality. MIL-STD-202 Method213 Condition F C/C To meet the initial specification. Peak value 1,500 G D.F. : To meet the initial specification. Normal duration 0.5 ms 10 Mechanical Shock Velocity change 15.4 ft/sec (4.7m/s) Direction and time 3 times each in X,Y, Z axis. Total 18 times Appearance : No visible damage. Preheating temperature : 15010 Resistance to C/C : 15% Preheating time 1 to 2 minute 11 Soldering Heat D.F. : To meet the initial specification. Solder temp. 2605 I.R. : To meet the initial specification. Dipping Time 101s Appearance : No abnormality. AEC-Q200-002 C/C To meet the initial specification. Connection Between terminals 12 ESD D.F. : To meet the initial specification. Direct Contact 8kV (150pF 2000) I.R. : To meet the initial specification. Times 1time Min. 75% of surface of the termination Solder Pb Free shall be covered with new solder. 13 Solderability Solder Temperature 245 5 Dipping Time 20.5s Appearance : No visible damage. The substrate shall be bend at rate of 1mm/s for 5 seconds. C/C : 15% Press bar Press Capacitor Substrate 14 Board Flex Bending capability* 452mm 452mm Support Bending capability 1mm or 2mm No visible damage. Substrate Terminal Strength 17.7N 15 601 seconds (SMD) Capacitor *CR : Rated Capacitance(F) Product specifications in this catalog are subject to change without notice.Request our product specifications before purchase and/or use. Please use our products based on the information contained in this catalog and product specifications. 20 CAT. No. E1002Z