Soldering and Desoldering Tips Important notice: special care for soldering tips Hand soldering operators are happy when their soldering tips last a long time and continue to solder well. Soldering tips that do not allow the solder to melt rapidly due to excess oxidation clearly disrupt productivity Special care of the soldering tip should be taken in order to solder efciently. Important Facts: 1. When a soldering tip remains hot for a long period of time, the tip will oxidize or blacken. An oxidized tip will no longer wet or melt solder properly. 2. The higher the working temperature of the soldering tip, the faster this oxidation will take place and tip lifetime will be shorter. 3. Soldering irons that automatically go into a lower stand-by temperature increase tip life. 4. The oxidation of the tip will be very rapid if the tip is left cook- ing without molten solder covering the tip end. It happens, for The ERSA Tip-Reactivator al- example, if the tip is not wettned with solder right after cleaning lows the regeneration of oxidized it. soldering tips. It is environmen- tally safe, free of lead and halo- 5. Excessive mechanical force during soldering will shorten the tip gens and func-tions even at low life. soldering tip temperatures. For 6. Proper care of the tip will greatly increase tip life. this purpose the heated soldering tip is wiped on the surface of the 7. Lead-free soldering requires higher temperatures, is more ag- regeneration compound. gressive to the tip and will always lead to shorter tip life. Nickel-plating Special Care: The base material made of highly conductive electrolytic copper ensures unhindered heat 1. Always clean the tip by wiping on a slightly wet sponge after transfer from the heating element to the each use. Alternatively, tips can be dry cleaned using wire ERSADUR LF coating mesh. 2. Always put fresh solder onto the end of the tip BEFORE putting ERSADUR LF coating (up to 600 micron) of iron-plating (subject to the tip back into the iron holder. type of tip) is factory pre-tinned with lead-free solder at working 3. Always use lowest working temperature possible. end 4. Never leave an iron cooking unattended for some time. Always set iron into automatic stand-by if possible or turn-off Nickel-plating when not in use. 5. Never use excessive mechanical force when soldering. Iron-plating 6. Soldering tip oxidation can be easily removed if detected early. Early detection and removal will greatly increase tip life. Chrome-plating prevents corrosion and solder collection on undesirable spots 7. Tip oxidation removal or tip refurbishing is accomplished in 4 consecutive steps: a. clean on damp sponge, b. clean with wire Cross-section of an ERSADUR soldering tip, non-scale representation brush, c. using a Tip re-activator chemical, and d. re-tinning using proper ux cored solder wire. ERSADUR LF soldering tips to process lead-free solders Conventional soldering tips can also be used for lead-free solders. Since lead-free soldering requires higher process temperatures, and due to the fact that lead-free solder is more aggressive to the soldering tip, the tips service life is shorter. ERSADUR LF solder- ing tips have an increased layer of iron, which increases tip life. Consequently they are especially suitable for lead-free soldering. 36 37Your Guide For: 422 ERSADUR Desoldering Tip Series DIGITAL 2000 A 0422FD10 0422ED 0422FD3 with Chip tool MICRO-CON 60 iA SMD Desoldering Pincette 40 REWORK 80 SMD 8000 4 mm, for e.g. SO 8 GT/14 GT/16GT 6 mm, for e.g. SOIC 8 7,5 mm, for e.g. SOIC 12 / SOT 23 SMT UNIT 60 AC / A with Chip tool / 0422FD1 0422FD4 0422FD2 SMD Desoldering Pincette 40 10 mm, for e.g. SOIC 16 12.5 mm, for e.g. SOIC 20 15 mm, for e.g. SOIC 24 0422FD5 0422FD6 0422FD7 17.5 mm, for e.g. SOIC 28 20 mm, for e.g. SOIC 32 25 mm, for e.g. SOIC 40 0422FD8 0422FD9 0422QD5 27.5 mm, for components of 27.5 mm 40 mm, for components of 40 mm side length side length 90, length 10 mm, for e.g. PLCC 20 0422QD1 0422QD6 0422QD3 90, length 15 mm, for e.g. QFP, TQFP and 90, length 12.5 mm, for e.g. PLCC 28 TQFP 0T25 90, length 17.5 mm, for e.g. PLCC 44 0422QD4 0422QD2 0422QD7 90, length 20 mm, for e.g. PLCC 52 90, length 25 mm, for e.g. PLCC 68 90, length 30 mm, for e.g. PLCC 84 0422RD1 0422RD2 0422MD length 22.5 x 16.5 mm, for e.g. QFP 100 length 15 x 12.5 mm, for e.g. PLCC 32 ellipse, for MELF and MINIMELF 0422SD* *Please note: The desoldering tips 0422SD must be used in combination with the tip turn protection set (see page 24) to ensure good results. Tip turn protection set for TC 40 desoldering pincette and Desoldering Pincette 40 on request. for MICROMELF 40 41