LD10YC226KAB2A500 Kyocera AVX

MLCC Tin/Lead Termination B X7R General Specifications AVX Corporation will support those customers for commercial and military Multilayer Ceramic Capacitors with a termination consisting of 5% minimum lead. This termination is indicated by the use of a B in the 12th position of the AVX Catalog Part Number. This fulfills AVXs commitment to providing a full range of products to our customers. AVX has provided in the following pages a full range of values that we are currently offering in this special B termination. Please contact the factory if you require additional information on our MLCC Tin/ Lead Termination B products. PART NUMBER (SEE PAGE 4 FOR COMPLETE PART NUMBER EXPLANATION) LD05 5 C 101 J A B 2 A Size Voltage Dielectric Capacitance Failure Terminations Packaging Special Capacitance LD03 - 0603 6.3V = 6 X7R = C Code (In pF) Rate B = 5% min lead 2 = 7 Reel Code Tolerance LD04 - 0504* 10V = Z 2 Sig. Digits + A = Not X = FLEXITERM 4 = 13 Reel A = Std. B = .10 pF (<10pF) with 5% min LD05 - 0805 16V = Y Number of Applicable Product C = .25 pF (<10pF) Contact Factory lead** LD06 - 1206 25V = 3 Zeros D = .50 pF (<10pF) For LD10 - 1210 35V = D F = 1% ( 10 pF) Multiples* LD12 - 1812 50V = 5 **X7R only G = 2% ( 10 pF) LD13 - 1825 100V = 1 J = 5% LD14 - 2225 200V = 2 K = 10% LD20 - 2220 500V = 7 M = 20% *LD04 has the same CV ranges as LD03. See FLEXITERM section for CV options NOTE: Contact factory for availability of Tolerance Options for Specific Part Numbers. Contact factory for non-specified capacitance values. The Important Information/Disclaimer is incorporated in the catalog where these specifications came from or available online at www.avx.com/disclaimer/ by reference and should be reviewed in full before placing any order. 47 112916MLCC Tin/Lead Termination B X7R Specifications and Test Methods Parameter/Test X7R Specification Limits Measuring Conditions Operating Temperature Range -55C to +125C Temperature Cycle Chamber Capacitance Within specified tolerance 10% for 50V DC rating Freq.: 1.0 kHz 10% 12.5% for 25V DC rating Voltage: 1.0Vrms .2V Dissipation Factor 12.5% for 25V and 16V DC rating 12.5% for 10V DC rating 100,000M or 1000M - F, Charge device with rated voltage for Insulation Resistance whichever is less 120 5 secs room temp/humidity Charge device with 250% of rated voltage for 1-5 seconds, w/charge and discharge current Dielectric Strength No breakdown or visual defects limited to 50 mA (max) Note: Charge device with 150% of rated voltage for 500V devices. Appearance No defects Deflection: 2mm Capacitance Test Time: 30 seconds 12% Variation Resistance to Flexure Dissipation Meets Initial Values (As Above) Stresses Factor Insulation Initial Value x 0.3 Resistance 95% of each terminal should be covered Dip device in eutectic solder at 230 5C Solderability with fresh solder for 5.0 0.5 seconds Appearance No defects, <25% leaching of either end terminal Capacitance 7.5% Variation Dip device in eutectic solder at 260C for 60 Dissipation Resistance to Meets Initial Values (As Above) seconds. Store at room temperature for 24 2 Factor Solder Heat hours before measuring electrical properties. Insulation Meets Initial Values (As Above) Resistance Dielectric Meets Initial Values (As Above) Strength Appearance No visual defects Step 1: -55C 2 30 3 minutes Capacitance 7.5% Step 2: Room Temp 3 minutes Variation Dissipation Meets Initial Values (As Above) Step 3: +125C 2 30 3 minutes Thermal Shock Factor Insulation Meets Initial Values (As Above) Step 4: Room Temp 3 minutes Resistance Dielectric Repeat for 5 cycles and measure after Meets Initial Values (As Above) Strength 24 2 hours at room temperature Appearance No visual defects Capacitance 12.5% Charge device with 1.5 rated voltage ( 10V) in Variation test chamber set at 125C 2C Dissipation for 1000 hours (+48, -0) Initial Value x 2.0 (See Above) Load Life Factor Insulation Remove from test chamber and stabilize at room Initial Value x 0.3 (See Above) Resistance temperature for 24 2 hours before measuring. Dielectric Meets Initial Values (As Above) Strength Appearance No visual defects Capacitance 12.5% Store in a test chamber set at 85C 2C/ 85% Variation 5% relative humidity for 1000 hours Dissipation (+48, -0) with rated voltage applied. Initial Value x 2.0 (See Above) Load Factor Humidity Remove from chamber and stabilize at room Insulation Initial Value x 0.3 (See Above) temperature and humidity for Resistance 24 2 hours before measuring. Dielectric Meets Initial Values (As Above) Strength The Important Information/Disclaimer is incorporated in the catalog where these specifications came from or available online at www.avx.com/disclaimer/ by reference and should be reviewed in full before placing any order. 48 112916