BLM18DN151SH1D Murata

Reference Only Spec.No.JENF243A-9159A-01 P1/8 Chip Ferrite Bead BLM18DNSH1D Murata Standard Reference Specification AEC-Q200 1.Scope This reference specification applies to Chip Ferrite Bead BLM18DN SH series for Automotive Electronics based on AEC-Q200. 2.Part Numbering (ex.) BL M 18 DN 601 S H 1 D (1) (2) (3) (4) (5) (6) (7) (8) (9) (1)Product ID (4)Characteristics (7)Category(for Automotive Electronics) (2)Type (5)Typical Impedance at 100MHz (8)Numbers of Circuit (3)Dimension (L) (6)Performance (9)Packaging (D:Taping) 3.Rating (*1) Impedance () DC Resistance Rated Current (*1) (refer to below comment) ( max.) (mA) (refer to below comment) Customer MURATA ESD Part Number Part Number Rank Values at at Initial at 100MHz at 1GHz After 85 125 Values Testing BLM18DN151SH1D 15025% 40030% 1400 900 0.120 0.140 BLM18DN151SH1B BLM18DN221SH1D 22025% 65030% 1000 650 0.210 0.255 BLM18DN221SH1B (*2) 3 BLM18DN381SH1D 38025% 110030% 850 550 0.325 0.390 BLM18DN381SH1B BLM18DN601SH1D 60025% 150030% 700 450 0.435 0.525 BLM18DN601SH1B Operating Temperature : -55C to +125C Storage Temperature : -55C to +125C (*1) Standard Testing Conditions < Unless otherwise specified > < In case of doubt > Temperature : Ordinary Temp. (15 C to 35 C ) Temperature : 20C2 C Humidity : Ordinary Humidity (25%(RH) to 85%(RH)) Humidity : 60%(RH) to 70%(RH) Atmospheric pressure : 86kPa to 106kPa (*2) Maximum Withstand Voltage 4000 V (DC) to 6000 V (DC) Rated current at 85C (Notes) Rated Current is derated as right figure Rated current depending on the operating temperature. at 125C 0 85 125 4.Style and Dimensions Operating Temperature (C) 1.60.15 0.80.15 Equivalent Circuit Resistance element becomes 0.40.2 () dominant at high frequencies. : Electrode Unit Weight (Typical value) 0.004g (in mm) MURATA MFG.CO.,LTD. 0.80.15 Rated Current (A)Reference Only Spec.No.JENF243A-9159A-01 P2/8 5.Marking No marking. 6.Specifications 6-1.Electrical Performance No. Item Specification Test Method 6-1-1 Impedance Meet item 3. Measuring Frequency : 100MHz1MHz,1GHz1MHz Measuring Equipment : KEYSIGHT 4291A or the equivalent Test Fixture : KEYSIGHT 16192A or the equivalent 6-1-2 DC Resistance Meet item 3. Measuring Equipment : Digital multi meter Except resistance of the Substrate and Wire 6-2.Mechanical Performance (based on Table 13 for FILTER EMI SUPPRESSORS/FILTERS) AEC-Q200 Rev.D issued June. 1 2010 AEC-Q200 Murata Specification / Deviation No.Stress Test Method 3 High 1000hours at 125 deg C Meet Table A after testing. Temperature Set for 24hours Table A Appearance No damage Exposure at room temperature, then measured. ImpedanceChange Within 50% (at 100MHz) DC Resistance Meet item 3. 4 Temperature Cycling 1000cycles Meet Table A after testing. -55 deg C to +125 deg C Table B Appearance No damage Set for 24hours ImpedanceChange at room temperature, Within 30% (at 100MHz) then measured. DC Resistance Meet item 3. 5 Destructive Per EIA469 No defects Physical Analysis No electrical tests 7 Biased Humidity 1000hours at 85 deg C, 85%RH Meet Table A after testing. Apply max rated current. 8 Operational Life Apply 125 deg C 1000hours Meet Table A after testing. Set for 24hours at room temperature, then measured 9 External Visual Visual inspection No abnormalities 10 Physical Dimension Meet ITEM 4 No defects Style and Dimensions 12 Resistance Per MIL-STD-202 Method 215 Not Applicable to Solvents 13 Mechanical Shock Per MIL-STD-202 Method 213 Meet Table B after testing. Condition F: 1500g s(14.7N)/0.5ms/Half sine 14 Vibration 5g s(0.049N) for 20 minutes,Meet Table B after testing. 12cycles each of 3 oritentations Test from 10-2000Hz. 15 Resistance Solder temperature Pre-heating: 150C +/-10 deg C, 60s to 90s to Soldering Heat 260C+/-5 deg C Immersion time 10s Meet Table A after testing. 17 ESD Per AEC-Q200-002 ESD Rank: Meet Item 3 (Rating) Meet Table A after testing. 18 Solderability Per J-STD-002 Method b : Not Applicable 95% of the terminations is to be soldered. 19 Electrical Measured : Impedance No defects Characterization MURATA MFG.CO.,LTD.