Soft Termination Chip Multilayer Ceramic Capacitors for Automotive
GCJ188R72A104KA01_ (0603, X7R:EIA, 0.1uF, DC100V)
_: packaging code Reference Sheet
1.Scope
This product specification is applied to Soft Termination Chip Multilayer Ceramic Capacitors used for Automotive Electronic equipment.
2.MURATA Part NO. System
(Ex.)
GCJ 18 8 R7 2A 104 K A01 D
(1)L/W (2)T
(3)Temperature (4)Rated (5)Nominal (6)Capacitance (7)Muratas Control
(8)Packaging Code
Dimensions Dimensions
Characteristics Voltage Capacitance Tolerance Code
3. Type & Dimensions
(Unit:mm)
(1)-1 L (1)-2 W (2) T e g
1.60.2 0.80.1 0.80.1 0.2 to 0.5 0.5 min.
4.Rated value
(3) Temperature Characteristics
Specifications and Test
(4) (6)
(Public STD Code):X7R(EIA)
(5) Nominal Methods
Rated Capacitance
Temp. coeff Temp. Range Capacitance (Operating
Voltage Tolerance
Temp. Range)
orCap. Change (Ref.Temp.)
-55 to 125 C
-15 to 15 % DC 100 V 0.1 uF 10 % -55 to 125 C
(25 C)
Soldering Method
Reflow
5.Package
mark (8) Packaging Packaging Unit
f180mm Reel
D 4000 pcs./Reel
PAPER W8P4
f330mm Reel
J 10000 pcs./Reel
PAPER W8P4
Product specifications in this catalog are as of May.15,2018,and are subject to change or obsolescence without notice.
Please consult the approval sheet before ordering.
Please read rating and !Cautions first.
GCJ188R72A104KA01-01 1AEC-Q200 Murata Standard Specification and Test Methods
No AEC-Q200 Test Item Specification. AEC-Q200 Test Method
1 Pre-and Post-Stress
-
Electrical Test
2 High Temperature The measured and observed characteristics should satisfy the Solder the capacitor on the test substrate(glass epoxy board).
Exposure (Storage) specifications in the following table. Set the capacitor for 1000+/-12h at 150+/-3.
Appearance No marking defects Set for 24+/-2h at room temperature, then measure.
Capacitance Within +/-12.5%
Change Initial measurement for high dielectric constant type
D.F. Within the specified initial value. Perform a heat treatment at 150+0/-10 for 1h and then sit
for 24+/-2h at room temperature.Perform the initial measurement.
Insulation Within the specified initial value.
Resistance
25
3 Temperature Cycling The measured and observed characteristics should satisfy the Solder the capacitor on the test substrate(glass epoxy board).
specifications in the following table. Perform the 1000 cycles test according to the four heat treatments
Appearance No marking defects listed in the following table.
Set for 24+/-2h at room temperature, then measure.
Step 1 2 3 4
Capacitance Within +/-7.5%
Temp. Room Room
Min.Operating Temp.+0/-3 Max.Operating Temp. +3/-0
Change
( C) Temp. Temp.
Time
15+/-3 1 15+/-3 1
D.F. Within the specified initial value.
(min.)
Insulation Within the specified initial value. Initial measurement
Resistance Perform a heat treatment at 150+0/-10 for 1h and then sit
25 for 24+/-2h at room temperature.
Perform the initial measurement.
4 Destructive No defects or abnormalities Per EIA-469
Physical Analysis
5 Moisture Resistance The measured and observed characteristics should satisfy the Solder the capacitor on the test substrate(glass epoxy board).
specifications in the following table. Apply the 24h heat (25 to 65) and humidity (80%RH to 98%RH)
Appearance No marking defects treatment shown below, 10 consecutive times.
Set for 24+/-2h at room temperature, then measure.
Humidity Humidity
Temperature
8098% 8098%
Capacitance Within +/-10.0%
Humidity Humidity Humidity
()
9098% 9098% 9098%
Change
70
65
60
D.F. Within the specified initial value.
55
50
45
40
35
Insulation Within the specified initial value.
30
25
Resistance
+10
20
25 - 2
15
10
5
Initial measuremt
0
-5
-10
One cycle 24hours
0 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24
Hours
Initial measurement
Perform a heat treatment at 150+0/-10 for 1h and then sit
for 24+/-2h at room temperature.
Perform the initial measurement.
6 Biased Humidity The measured and observed characteristics should satisfy the Solder the capacitor on the test substrate(glass epoxy board).
specifications in the following table. Apply the rated voltage and 1.3+0.2/-0Vdc (add 6.8k resister)
Appearance No marking defects at 85+/-3 and 80%RH to 85%RH humidity for 1000+/-12h.
The charge/discharge current is less than 50mA.
Capacitance Within +/-12.5% Remove and set for 24+/-2h at room temperature, then measure.
Change
Initial measurement
D.F. Within the specified initial value. Perform a heat treatment at 150+0/-10 for 1h and then sit
for 24+/-2h at room temperature.
Perform the initial measurement.
Insulation More than 1,000M or 50F
Resistance (Whichever is smaller)
25