Chip Multilayer Ceramic Capacitors for Automotive GCM2199E2A132KA05 (0805, ZLM:EIA, 1300pF, DC100V) : packaging code Reference Sheet 1.Scope This product specification is applied to Chip Multilayer Ceramic Capacitors used for Automotive Electronic equipment. 2.MURATA Part NO. System (Ex.) G C M 21 9 9E 2A 132 K A05 D (2)T (1)L/W (3)Temperature (4)Rated (6)Capacitance (7)Muratas Control (8)Packaging Code (5)Nominal Capacitance Dimensions Dimensions Characteristics Voltage Tolerance Code 3. Type & Dimensions (Unit:mm) (1)-1 L (1)-2 W (2) T e g 2.00.15 1.250.15 0.850.1 0.2 to 0.7 0.7 min. 4.Rated value (3) Temperature Characteristics Specifications and Test (4) (6) (Public STD Code):ZLM(EIA) (5) Nominal Methods Rated Capacitance Temp. coeff Temp. Range Capacitance (Operating Voltage Tolerance Temp. Range) or Cap. Change (Ref.Temp.) -4700 +1000/-2500ppm/ (-55 to -40 ) -5350 +750/-750ppm/ (-40 to +20 ) -55 to 125 C DC 100 V 1300 pF 10 % -55 to 125 C -4700 +500/-500ppm/ (+20 to +85 ) (20 C) -4700 +2000/-1000ppm/ (+85 to +125 ) 5.Package mark (8) Packaging Packaging Unit f180mm Reel D 4000 pcs./Reel PAPER W8P4 f330mm Reel J 10000 pcs./Reel PAPER W8P4 Product specifications in this catalog are as of May.23,2018,and are subject to change or obsolescence without notice. Please consult the approval sheet before ordering. Please read rating and Cautions first. GCM 2 1 9 9 E2 A1 3 2 KA0 5 - 0 1 1AEC-Q200 Murata Standard Specification and Test Methods AEC-Q200 Test Method No AEC-Q200 Test Item Specification. Pre-and Post-Stress 1 - Electrical Test 2 High Temperature The measured and observed characteristics should satisfy the Solder the capacitor on the test substrate(glass epoxy board). Exposure (Storage) specifications in the following table. Set the capacitor for 1000+/-12h at 150+/-3. Appearance No marking defects Set for 24+/-2h at room temperature, then measure. Capacitance Within +/-7.5% Change D.F. 0.02 max. I.R. Within the specified initial value. 25 3 Temperature Cycling The measured and observed characteristics should satisfy the Solder the capacitor on the test substrate(glass epoxy board). specifications in the following table. Perform cycle test according to the four heat treatments listed Appearance No marking defects in the following table. Set for 24+/-2h at room temperature, then measure. Capacitance Within +/-7.5% Step Time(min) 1000 Cycles Change 1 15+/-3 -55+0/-3 D.F. 0.01 max. 2 1 Room 3 15+/-3 125+3/-0 4 1 Room I.R. Within the specified initial value. 25 4 Destructive No defects or abnormalities Per EIA-469. Physical Analysis 5 Moisture Resistance The measured and observed characteristics should satisfy the Solder the capacitor on the test substrate(glass epoxy board). Apply the 24h heat (25 to 65) and humidity (80%RH to 98%RH) specifications in the following table. treatment shown below, 10 consecutive times. Appearance No marking defects Set for 24+/-2h at room temperature, then measure. Capacitance Within +/-12.5% Humidity Humidity Temperature Change 8098% 8098% Humidity Humidity Humidity () 9098% 9098% 9098% 70 65 D.F. 0.02 max. 60 55 50 45 40 I.R. Within the specified initial value. 35 30 25 25 +10 20 - 2 15 10 5 Initial measuremt 0 -5 -10 One cycle 24hours 0 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 Hours 6 The measured and observed characteristics should satisfy the Biased Humidity Solder the capacitor on the test substrate(glass epoxy board). specifications in the following table. Apply the rated voltage and 1.3+0.2/-0vdc (add 6.8k resister) at 85+/-3 and 80%RH to 85%RH humidity for 1000+/-12h. Appearance No marking defects The charge/discharge current is less than 50mA. Remove and set for 24+/-2h at room temperature, then measure. Capacitance Within +/-12.5% Change D.F. 0.02 max. I.R. More than 1,000M or 50F 25 (Whichever is smaller) JEMCGS-01644C 2