Chip Monolithic Ceramic Capacitor meet AEC-Q200 for Infotainment GRT188C81E105KE13 (0603, X6S, 1uF, DC25V) : packaging code Reference Sheet 1.Scope This product specification is applied to Chip Monolithic Ceramic Capacitor used for Car Multimedia, Car Interior, Car Comfort application and General Electronic equipment. Please contact us when using this product for any other applications than described in the above. Do not use these products in applications critical to passenger safety and car driving function (e.g. ABS, AIRBAG, etc.). 2.MURATA Part NO. System (Ex.) GRT 18 8 C8 1E 105 K E13 D (6)Capacitance (7)Muratas (1)L/W (2)T (3)Temperature (4)Rated (5)Nominal (8)Packaging Tolerance Control Code Dimensions Dimensions Characteristics Voltage Capacitance Code 3. Type & Dimensions (Unit:mm) (1)-1 L (1)-2 W (2) T e g 1.60.1 0.80.1 0.80.1 0.2 to 0.5 0.5 min. 4.Rated value (3) Temperature Characteristics Specifications and Test (4) (6) (Public STD Code):X6S(EIA) (5) Nominal Methods Rated Capacitance Capacitance (Operating Temp. coeff Temp. Range Voltage Tolerance Temp. Range) orCap. Change (Ref.Temp.) -55 to 105 C -22 to 22 % DC 25 V 1 uF 10 % -55 to 105 C (25 C) 5.Package mark (8) Packaging Packaging Unit f180mm Reel D 4000 pcs./Reel PAPER W8P4 f330mm Reel J 10000 pcs./Reel PAPER W8P4 Product specifications in this catalog are as of Apr.17,2015,and are subject to change or obsolescence without notice. Please consult the approval sheet before ordering. Please read rating and Cautions first. GRT188C81E105KE13-01 1AEC-Q200 Murata Standard Specification and Test Methods No AEC-Q200 Test Item Specifications. AEC-Q200 Test Method 1 Pre-and Post-Stress - Electrical Test 2 High Temperature The measured and observed characteristics should satisfy the Set the capacitor for 100012 hours at maximum operating temperature 3 . Exposure (Storage) specifications in the following table. Appearance No marking defects Set for 242 hours at room temperature, then measure. Capacitance R6, C8: Within 12.5% Change Dissipation R6, C8: 0.2 max. Factor Insulation 25F min. Resistance 3 Temperature Cycling The measured and observed characteristics should satisfy the Fix the capacitor to the supporting jig in the same manner and under specifications in the following table. the same conditions as (18). Perform the 1000 cycles test according Appearance No marking defects to the four heat treatments in the following table. Capacitance R6, C8: Within 7.5% Set for 242 hours at room temperature, then measure. Change Step 1 2 3 4 Dissipation R6, C8: 0.2 max. Temp. Room 85 +3/-0 (For R6) Room -55+0/-3 Factor (C) Temp. 105+3/-0 (For C8) Temp. Time 153 1 153 1 (min.) 50F min. Insulation Resistance Initial measurement for high dielectric constant type Perform a heat treatment at 150+0/-10 for one hour and then set for 242 hours at room temperature. Perform the initial measurement. 4 Destructive No defects or abnormalities Per EIA-469 Physical Analysis 5 Biased Humidity The measured and observed characteristics should satisfy the Apply the rated voltage and 1.3+0.2/-0vdc (add 6.8k resister) specifications in the following table. at 853 and 80 to 85% humidity for 100012 hours. Appearance No marking defects Remove and set for 242 hours at room temperature, then measure. Capacitance R6,C8: Within 12.5% The charge/discharge current is less than 50mA. Change Measurement after test for high dielectric constant type Dissipation R6,C8: 0.2 max Factor Perform a heat treatment at 150+0/10C for one hour and then let sit for 242 hours at room temperature, then measure. Insulation 5 F min. Resistance JEMCGS-01744J 2