Only Reflow Soldering 10 Terminals Low ESL Chip Multilayer Ceramic Capacitors for General Purpose LLM215R70J224MA11 (0805, X7R:EIA, 0.22uF, DC6.3V) : packaging code Reference Sheet 1.Scope This product specification is applied to 10 Terminals Low ESL Chip Multilayer Ceramic Capacitors used for General Electronic equipment. This product is applied for Only Reflow Soldering. 2.MURATA Part NO. System (Ex.) LLM 21 5 R7 0J 224 M A11 L (1)L/W (2)T (3)Temperature (4)Rated (5)Nominal (6)Capacitance (7)Muratas Control (8)Packaging Code Dimensions Dimensions Characteristics Voltage Capacitance Tolerance Code 3. Type & Dimensions a)Equivalent Circuit (Unit:mm) (1)-1 L (1)-2 W (2) T p 2.00.1 1.250.1 0.5+0.05/-0.1 0.50.05 4.Rated value (3) Temperature Characteristics Specifications and Test (4) (6) (Public STD Code):X7R(EIA) (5) Nominal Methods Rated Capacitance (Operating Temp. coeff Temp. Range Capacitance Voltage Tolerance Temp. Range) orCap. Change (Ref.Temp.) -55 to 125 C -15 to 15 % DC 6.3 V 0.22 uF 20 % -55 to 125 C (25 C) 5.Package mark (8) Packaging Packaging Unit f180mm Reel L 4000 pcs./Reel EMBOSSED W8P4 f330mm Reel K 10000 pcs./Reel EMBOSSED W8P4 Product specifications in this catalog are as of Jun.8,2017,and are subject to change or obsolescence without notice. Please consult the approval sheet before ordering. Please read rating and Cautions first. LLM215R70J224MA11-01 1 Specifications and Test Methods Test Method No Item Specification (Ref. Standard:JIS C 5101, IEC60384 1 Rated Voltage Shown in Rated value. The rated voltage is defined as the maximum voltage which may be applied continuously to the capacitor. When AC voltage is superimposed on DC voltage, P-P O-P V or V , whichever is larger, should be maintained within the rated voltage range. 2 Appearance No defects or abnormalities. Visual inspection. 3 Dimension Within the specified dimensions. Using Measuring instrument of dimension. 4 Voltage proof No defects or abnormalities. Measurement Point : Between the terminations Test Voltage : 250% of the rated voltage Applied Time : 1s to 5 s Charge/discharge current : 50mA max. 5 Insulation Resistance(I.R.) C0.047F:More than 10000M Measurement Point : Between the terminations C0.047F:More than 500F Measurement Voltage : DC Rated Voltage C:Nominal Capacitance Charging Time : 2 min Charge/discharge current : 50mA max. Measurement Temperature : Room Temperature 6 Capacitance Shown in Rated value. Measurement Temperature : Room Temperature Capacitance Frequency Voltage C10F 1.0+/-0.1kHz 1.0+/-0.2Vrms * 7 Dissipation Factor (D.F.) W.V.:25Vdc min. : 0.025max. * For item LLA185 C7 0G 274 to 474, the capacitance should be W.V.:16/10Vdc : 0.035max. measured using a voltage of 0.5+/-0.1Vrms. W.V.:6.3Vdc max. : 0.05max. For item LLA185/215 C7 0G 473, the capacitance should be measured using a voltage of 0.5+/-0.2Vrms. 8 Temperature No bias R7 : Within +/-15% (-55C to +125C) The capacitance change should be measured after 5 min Characteristics R6 : Within +/-15% (-55C to +85C) at each specified temp. stage. of Capacitance C7 : Within +/-22% (-55C to +125C) Capacitance value as a reference is the value in step 3. Applying Voltage(Vdc) Step Temperature( C) 1 Reference Temp.+/-2 2 Min.Operating Temp.+/-3 3 Reference Temp.+/-2 No bias 4 Max.Operating Temp.+/-3 5 Reference Temp.+/-2 Initial measurement Perform a heat treatment at 150+0/-10C for 1h and then let sit for 24+/-2h at room temperature,then measure. 9 Adhesive Strength of No removal of the terminations or other defect Solder the capacitor on the test substrate (glass epoxy board). Termination should occur. Applied Force : 5N Holding Time : 10+/-1s Applied Direction : In parallel with the test substrate and vertical with the capacitor side. 10 Vibration Appearance No defects or abnormalities. Solder the capacitor on the test substrate (glass epoxy board). Capacitance Within the specified initial value. Kind of Vibration : A simple harmonic motion 10Hz to 55Hz to 10Hz (1min) D.F. Within the specified initial value. Total amplitude : 1.5mm This motion should be applied for a period of 2h in each 3 mutually perpendicular directions(total of 6h). JEMCAS-00670C 2