18900 Panduit Drive TDS: GMH3-A Tinley Park, IL 60487 Effective Date: 04APR17 Customer Service: 800-777- Revision: 3 3300 Technical Data Sheet Panduit Raised Panel Label This specification is intended to outline the physical and chemical properties of PANDUITs GMH3-A material and include the following printable material identifiers: Printable Material Suffixes AQT A0T A8T AMT AST AUT AWT *-30-ES PRODUCT SPECIFICATIONS: Description: Material is RoHS compliant (European Union directive 2002/95/EC). GMH3-A consists of a polyester film laminated to a microcellular foam backed high tack adhesive. Print Methods: This material is recommended for thermal transfer printing. Standard Colors: Blue, black, yellow, green, red, silver and orange. Thickness: 27 - 32 mils (ASTM D3652) Recommended Ribbons: RMR4BL-A, RMR4WH Service Temperature Range: -40F to 212F (-40C to 100C) Minimum Application Temperature: 50F (10C) Storage Conditions: Store at 70F (21C) and 50% Relative Humidity. PROPERTIES: PERFORMANCE: Peel Adhesion to: 100 oz/in (PSTC-101, 20 min dwell) -Stainless Steel 150 oz/in (PSTC-101, 24 hour dwell) 100 oz/in (PSTC-101, 20 min dwell) -Smooth ABS 150 oz/in (PSTC-101, 24 hour dwell) 100 oz/in (PSTC-101, 20 min dwell) -Powdercoated surface 150 oz/in (PSTC-101, 24 hour dwell) Tears (PSTC-101, 20 min dwell) -Polycarbonate Tears (PSTC-101, 24 hour dwell) 24+ hours (PSTC-107) Shear Test Tack 72.0 oz/in (PSTC-16) Samples were thermal transfer printed with RMR4BL-A, RMER*BL black resin ribbon and RMR*WH, RMER*WH white resin ribbon on the Panduit TDP43MY AND TDP43ME printer. Thermal transfer printed samples were tested as follows: UV Resistance: 12000 hours* no change observed (ASTM G154) Humidity Resistance: 1000 hours at 100F(37C) and 95% R.H, no visible change observed Page 1 of 4 2015 PANDUIT Corp TDS: GMH3-A 18900 Panduit Drive TDS: GMH3-A Tinley Park, IL 60487 Effective Date: 04APR17 Customer Service: 800-777- Revision: 3 3300 Technical Data Sheet *Test conducted in the QUV Weatherometer to assimilate 20 years of expected outdoor exposure under normal conditions. Long Term High Service Temperature: 1000 hours at 212F(100C), no visible change observed Long Term Low Service Temperature: 1000 hours at 40F(-40C), no visible change observed Abrasion Resistance: Taber abraser, CS-10 wheels/500 gm wt/175 cycles, no visible change observed (ASTM D3389). PROPERTIES FOR SOLAR APPLICATION: PERFORMANCE: Short term low temperature exposure: 30 days at -51C, no visible change observed Relative Lightfastness and weatherability: 1000 hours, no change observed (ASTM D3424, Method 4) Tensile Strength: MD: 3985 PSI (ASTM D3759) Elongation: MD: 150% (ASTM D3759) Tack: 9.2N (ASTM D2979) Flammability: 230 seconds (ASTM D1000) Adhesion: 44.7 oz/in (ASTM D3330) CHEMICAL/SOLVENT RESISTANCE: Thermal Transfer Print with Black Ribbon The testing was conducted at room temperature. Samples were thermal transfer printed with RMR4BL-A, RMER*BL black resin ribbon on the Panduit TDP43MY AND TDP43ME printer. Separate sets were conditioned for 24 hours before being immersed in the following solvents. Testing consisted of 5 cycles of 10 minute immersions in the specified chemical reagent followed by a 30 minute recovery period. After final immersion, samples were rubbed 10 times with a cotton swab saturated with the test fluid. Visual observations were noted for any smear or loss of legibility. Chemical/Solvent Visual Observation of Print without Visual Observation of print rub with rub Isopropyl alcohol No change No change Methyl Ethyl Ketone No change Loss of print legibility Alcohol mix* No change No change Gasoline No change No change Diesel No change No change Skydrol No change No change Mil 5606 oil No change No change 1,1,1-Trichloroethane No change No change 5% Sodium Hydroxide No change No change 10% Sulfuric acid solution No change No change Deionized water No change No change 10% Salt water solution No change No change n-Hexane No change No change Iso-octane No change No change Ethanol No change No change ASTM 3 oil No change No change Acetone No change No change Bleach No change No change Page 2 of 4 2015 PANDUIT Corp TDS: GMH3-A