18900 Panduit Drive TDS: GMUFR31 Tinley Park, IL 60487 Effective Date: 20MAR19 Customer Service: 800-777-3300 Revision: 5 Technical Data Sheet Fluid Resistant Heat Shrink Labels ANDUITs GMUFR31tubing This specification is intended to outline the physical and chemical properties of P material for wire identification and insulation purposes and include the following part numbers and printable material identifiers: Part Number Prefixes Part Number Suffixes HST-2 PRODUCT SPECIFICATIONS: Description: Material is RoHS compliant (European Union directive 2002/95/EC). GMUFR31 is a crosslinked, semi rigid, diesel resistant heat shrinkable thermal transfer printable polyolefin. This product meets the material and physical property requirements AMS-DTL-23053/6 Class 1 and NF F00-608 Class A & H when printed using RMER4BL-C thermal transfer ribbon. It will also meet SAE-AS5942, MIL-STD-883F Method 2015.13, Solutions A and D, and MIL-STD-202G Method 215K, Solutions A, and D. RMER4BL-C Recommended Ribbons: Yellow Standard Colors: Shrink Ratio: 3 to 1 1/8( 3.2mm) ID size is 2 to 1 shrink ratio Service Temperature Range: Minus 67F to 275F (Minus 55C to 135C) 0 0 Storage Conditions: Store at 70 F(21 C) and 50% Relative Humidity PROPERTIES: PERFORMANCE: Tensile Strength: 19MPa minimum (IEC 60684-2) Elongation Ultimate: 480% minimum (IEC 60684-2) 20 KV/mm minimum (IEC 243) Dielectric Strength: 14 1.2 x10 ohm cm Volume Resistivity: (IEC 60684-2 clause 23, section 23.4.2 & 23.4.4) 0 No dripping, cracking or flowing(ASTM D2671) Heat Shock 4 hours at 250 C: 0 Elongation 300% (IEC 60684-2, section 19.1) Heat Aging 168 hours at 175 C: Minus 10% maximum (IEC60684-2) Total Longitudinal Change: Water Absorption: 0.20% (NF F00-608 section 11.4.9 & ASTM D70) 0 Low Temperature Flexibility minus 55 C: No cracking (ASTM D2671) Page 1 of 4 2012 PANDUIT Corp TDS: GMUFR31 18900 Panduit Drive TDS: GMUFR31 Tinley Park, IL 60487 Effective Date: 20MAR19 Customer Service: 800-777-3300 Revision: 5 Technical Data Sheet Printability: Product meets print performance of 100 rubs (Taber abraser, CS-10 wheels, 100 cycles/250 gm wt) Flammability: Self-extinguishing < 30 sec(NF F00-608 Section 5.5.8, ASTM D2671 Procedure B) Specific gravity: 1.35 (ISO/R1183) 0 0 Shrink Temperature: 275 F (135 C) Minimum Oxygen Index: 24% minimum (NF T 51-071) QUV Outdoor Durability: Observations made at *3000 hours exposure showed no loss in legend or change in material (ASTM G154). Secant Modulus 2% 25,000 psi (172.4 Mpa) minimum (NF F 60684-2 clause 19.4 & ASTM D 882) Corrosion Related Items: Item Test or Procedure Result / Comments Corrosion ASTM D2671 B No Corrosion Copper Corrosion -Tensile NF 00-608 11.4.7 according to NF C 93-641 13 Mpa paragraph 3.3.7.2. Copper Corrosion - NF 00-608 11.4.7 according to NF C 93-641 240 % Elongation paragraph 3.3.7.2. Copper Corrosion -Visual NF 00-608 11.4.7 according to NF C 93-641 pass paragraph 3.3.7.2. Marking Performance: SAE-AS5942: Samples were tested heat shrunk. Print still legible after 20 eraser rubs with hard hand pressure. MIL-STD-202G Method 215K, Solution A and D: 3 cycles of 3 minute immersions in specified fluids followed by toothbrush rub after each immersion. Print still legible in all test fluids. MIL-STD-883F: M et hod 2015.13, Solution A and D: 3 cycles of 1 minute immersions in specified fluids followed by toothbrush rub after each immersion. Print still legible in all test fluids. *3000 hours aquates to 5 years of assimilated outdoor UV exposure. Page 2 of 4 2012 PANDUIT Corp TDS: GMUFR31