CL10C150JB81PNC Samsung

Specification of Automotive MLCC (Reference sheet) Supplier : Samsung electro-mechanics Samsung P/N : CL10C150JB81PNC Description : CAP, 15, 50V, 5%, C0G, 0603 Product : Multi-layer Ceramic Capacitor AEC-Q200 Qualified A. Dimension Dimension Size 0603 inch L 1.600.10 mm W 0.800.10 mm T 0.800.10 mm BW 0.300.20 mm B. Samsung Part Number CL 10 C 150 J B 8 1 P N C Series Samsung Multi-layer Ceramic Capacitor 0603 Size (inch code) L: 1.600.10 mm W: 0.800.10 mm Dielectric C0G Inner electrode Ni Capacitance 15 Termination Cu Capacitance 5% Plating Sn 100% (Pb Free) tolerance Product Automotive Rated Voltage 50 V Special code Normal Thickness 0.800.10 mm Packaging Cardboard Type, 7 Reel C. Reliability Test and Judgement condition Performance Test condition Appearance : No abnormal exterior appearance Unpowered, 1,000hrs Max. temperature High Temperature Capacitance Change : Within 2.5% or 0.25 Measurement at 242hrs after test conclusion Exposure whichever is larger Q : 700 min. IR : More than 10,000 or 500 Whichever is smaller Appearance : No abnormal exterior appearance 1,000Cycles Temperature Cycling Capacitance Change : Within 2.5% or 0.25 Measurement at 242hrs after test conclusion whichever is larger Q : 700 min. 1 cycle condition : -55+0/-3 (303min) Room Temp. (1min) IR : More than 10,000 or 500 125+3/-0 (303min) Room Temp. (1min) Whichever is smaller No Defects or abnormalities Per EIA 469 Destructive Physical Analysis Appearance : No abnormal exterior appearance 1,000hrs 85 /85%RH, Rated Voltage and 1.3~1.5V, Humidity Bias Capacitance Change : Within 2.5% or 0.25 Add 100kohm resistor whichever is larger Q : 149.95 min. The charge/discharge current is less than 50mA. IR : More than 500 or 25 Whichever is smaller Appearance : No abnormal exterior appearance 1,000hrs 125 , 200% Rated Voltage, High Temperature Capacitance Change : Within 3% or 0.3 Measurement at 242hrs after test conclusion Operating Life whichever is larger The charge/discharge current is less than 50mA. Q : 312.5 min. IR : More than 1,000 or 50 Whichever is smaller Performance Test condition No abnormal exterior appearance Microscope (10) External Visual Within the specified dimensions Using The calipers Physical Dimensions Appearance : No abnormal exterior appearance Three shocks in each direction should be applied along Mechanical Shock Capacitance Change : Within 2.5% or 0.25 3 mutually perpendicular axes of the test specimen (18 shocks) whichever is larger Peak value Duration Wave Velocity 1,500G 0.5ms Half sine 4.7m/sec Q, IR : Initial spec. Appearance : No abnormal exterior appearance 5g s for 20min., 12cycles each of 3 orientations, Vibration Capacitance Change : Within 2.5% or 0.25 Use 8 5 PCB 0.031 Thick 7 secure points on one long side whichever is larger and 2 secure points at corners of opposite sides. Parts mounted within 2 from any secure point. Test from 10~2,000 . Q, IR : Initial spec. Appearance : No abnormal exterior appearance Resistance to Preheating : 150 for 60~120 sec. Capacitance Change : Within 2.5% or 0.25 Solder pot : 2605 , 101sec. Solder Heat whichever is larger Q, IR : Initial spec. Appearance : No abnormal exterior appearance ESD AEC-Q200-002 or ISO/DIS10605 Capacitance Change : Within 2.5% or 0.25 whichever is larger Q, IR : Initial spec. 95% of the terminations is to be soldered Solderability a) Preheat at 155 for 4 hours, Immerse in solder for 5s at 2455 evenly and continuously b) Steam aging for 8 hours, Immerse in solder for 5s at 2455 c) Steam aging for 8 hours, Immerse in solder for 120s at 2605 solder : a solution ethanol and rosin Capacitance : Within specified tolerance The Capacitance / D.F. should be measured at 25 , Electrical Q : 700 min. 1 10%, 0.5~5 Vrms Characterization More than 100,000 or 1,000 I.R. should be measured with a DC voltage not exceeding IR(25 ) : Whichever is smaller. Rated Voltage 25 , 125 for 60~120 sec. IR(125 ) : More than 10,000 or 100 Whichever is smaller. Dielectric Strength Dielectric Strength : 300% of the rated voltage for 1~5 seconds Appearance : No abnormal exterior appearance Bending to the limit, 3 for 60 seconds Board Flex Capacitance Change : Within 5% or 0.5 whichever is larger Appearance : No abnormal exterior appearance 10 N, for 60 sec. Terminal Capacitance Change : Within 2.5% or 0.25 Strength(SMD) whichever is larger Destruction value should be exceed 20 N Beam speed : 0.50.05 /sec Beam Load C0G Temperature From -55 to 125 , Capacitance change should be within 030ppm/ Characteristics D. Recommended Soldering method : Reflow ( Reflow Peak Temperature : 260 +0/-5 , 30sec. ), Meet IPC/JEDEC J-STD-020 D Standard Product specifications included in the specifications are effective as of March 1, 2013. Please be advised that they are standard product specifications for reference only. We may change, modify or discontinue the product specifications without notice at any time. So, you need to approve the product specifications before placing an order. Should you have any question regarding the product specifications, please contact our sales personnel or application engineers.