Specification of Automotive MLCC Samsung P/N : CL21B223KC65PNC Supplier : Samsung electro-mechanics CAP, 22, 100V, 10%, X7R, 0805 Product : Multi-layer Ceramic Capacitor Description : AEC-Q 200 Specified A. Samsung Part Number CL 21 B 223 K C 6 5 P N C Samsung Multi-layer Ceramic Capacitor Series 0805 (inch code) L: 2.0 0.1 mm W: 1.25 0.1 mm Size Dielectric X7R Inner electrode Ni , Open mode Capacitance 22 Termination Cu , Ag-epoxy Capacitance 10 % Plating Sn 100% (Pb Free) tolerance Product Automotive Rated Voltage 100 V Grade code Standard Thickness 0.6 0.1 mm Packaging Cardboard Type, 7 reel B. Reliablility Test and Judgement condition Performance Test condition High Temperature Appearance : No abnormal exterior appearance Unpowered, 1000hrs T=150 Exposure Capacitance Change : Within 10% Measurement at 242hrs after test conclusion Tan : 0.03 max IR : More than 10,000 or 500 Whichever is Smaller Appearance : No abnormal exterior appearance Temperature Cycling 1000Cycles Capacitance Change : Within 10% Measurement at 242hrs after test conclusion Tan : 0.03 max 1 cycle condition : IR : More than 10,000 or 500 -55+0/-3(153min) -> Room Temp(1min.) Whichever is Smaller -> 125+3/-0(153min) -> Room Temp(1min.) Destructive Physical No Defects or abnormalities Per EIA 469 Analysis Moisture Resistance Appearance : No abnormal exterior appearance 10Cycles, t=24hrs/cycle Capacitance Change : Within 12.5% Heat (25~65) and humidity (80~98%), Unpowered Tan : 0.03 max measurement at 242hrs after test conclusion IR : More than 10,000 or 500 Whichever is Smaller Appearance : No abnormal exterior appearance Humidity Bias 1000hrs 85/85%RH, Rated Voltate and 1.3~1.5V, Capacitance Change : Within 12.5% Add 100kohm resistor Tan : 0.035 max Measurement at 242hrs after test conclusion The charge/discharge current is less than 50mA. IR : More than 500 or 25 Whichever is Smaller High Temperature Appearance : No abnormal exterior appearance 1000hrs TA=125, 200% Rated Voltage, Operating Life Capacitance Change : Within 12.5% Measurement at 242hrs after test conclusion Tan : 0.035 max The charge/discharge current is less than 50mA. IR : More than 1000 or 50 Whichever is SmallerPerformance Test condition External Visual No abnormal exterior appearance Microscope (10) Physical Dimensions Within the specified dimensions Using The calipers Appearance : No abnormal exterior appearance Mechanical Shock Three shocks in each direction should be applied along Capacitance Change : Within 10% 3 mutually perpendicular axes of the test specimen (18 shocks) Peakvalue Duration Wave Velocity Tan , IR : initial spec. 1,500G 0.5ms Half sine 4.7m/sec. Vibration Appearance : No abnormal exterior appearance 5g s for 20min., 12cycles each of 3 orientations, Capacitance Change : Within 10% Use 8 5 PCB 0.031 Thick 7 secure points on one long side Tan , IR : initial spec. and 2 secure points at corners of opposite sides. Parts mounted within 2 from any secure point. Test from 10~2000. Resistance to Appearance : No abnormal exterior appearance Solder pot : 2605, 101sec. Solder Heat Capacitance Change : Within 10% Tan , IR : initial spec. Appearance : No abnormal exterior appearance Thermal Shock -55/+125. Capacitance Change : Within 10% Note: Number of cycles required-300, Tan , IR : initial spec. Maximum transfer time-20 sec, Dwell time-15min. Air-Air Appearance : No abnormal exterior appearance AEC-Q200-002 ESD Capacitance Change : Within 10% Tan , IR : initial spec. Solderability 95% of the terminations is to be soldered a) Preheat at 155 for 4 hours, Immerse in solder for 5s at 2455 evenly and continuously b) Steam aging for 8 hours, Immerse in solder for 5s at 2455 c) Steam aging for 8 hours, Immerse in solder for 120s at 2605 solder : a solution ethanol and rosin Electrical Capacitance : Within specified tolerance The Capacitance /D.F. should be measured at 25, Characterization Tan (DF) : 0.025 max. 110%, 1.00.2Vrms IR(25) : More than 10,000 or 500 I.R. should be measured with a DC voltage not exceeding IR(125) : More than1,000 or 10 Rated Voltage 25, 125 for 60~120 sec. Whichever is Smaller Dielectric Strength Dielectric Strength : 250% of the rated voltage for 1~5 seconds Board Flex Appearance : No abnormal exterior appearance Bending to the limit (2) for 5 seconds Capacitance Change : Within 10% Terminal Appearance : No abnormal exterior appearance 18N, for 601 sec. Strength(SMD) Capacitance Change : Within 10% Beam Load Destruction value should not be exceed Beam speed Chip Length < 2.5 0.50.05/sec a) Chip Thickness > 0.5 : 20N b) Chip Thickness 0.5 : 8N X7R Temperature Characterisitcs (From -55 to 125, Capacitance change shoud be within 15%) C. Recommended Soldering method : Reflow ( Reflow Peak Temperature : 260+0/-5, 10sec. Max ) Meet IPC/JEDEC J-STD-020 D Standard * For the more detail Specification, Please refer to the Samsung MLCC catalogue.