(Reference sheet)
SPECIFICATION
CL32B106KLULNNF
Supplier : Samsung electro-mechanics Samsung P/N :
CAP, 10uF, 35V, 10%, X7R, 1210
Product : Multi-layer Ceramic Capacitor Description :
A. Samsung Part Number
CL 32 B 106 K L U L N N F
Series Samsung Multi-layer Ceramic Capacitor
Size 1210 (inch code) L : 3.20 0.30 W : 2.50 0.20
Thickness division Low profile
Dielectric X7R Inner electrode Ni
10 uF Cu
Capacitance Termination
Sn 100%
Capacitance 10 % Plating (Pb Free)
tolerance Product Normal
Rated Voltage 35 V Special Reserved for future use
Thickness 1.80 0.20 Packaging Embossed Type, 13" reel
B. Structure & Dimension
Dimension()
Samsung P/N
LTW BW
CL32B106KLULNNF 3.20 0.30 2.50 0.20 1.80 0.20 0.60 0.30C. Samsung Reliablility Test and Judgement Condition
Judgement Test condition
Capacitance Within specified tolerance 1 10% / 1.00.2Vrms
*A capacitor prior to measuring the capacitance is heat
Tan (DF) 0.1 max. treated at 150+0/-10 for 1hour and maintained in
ambient air for 242 hours.
Insulation 10,000Mohm or 100Mohm Rated Voltage 60~120 sec.
Resistance Whichever is smaller
Appearance No abnormal exterior appearance Microscope (10)
250%
Withstanding No dielectric breakdown or of the rated voltage
Voltage mechanical breakdown
Temperature X7R
Characteristics
(From-55 to 125 , Capacitance change should be within 15%)
Adhesive Strength No peeling shall be occur on the 500gf, for 101 sec.
of Termination terminal electrode
Bending Strength Capacitance change : within 12.5% Bending to the limit (1)
with 1.0mm/sec.
Solderability More than 75% of terminal surface SnAg3.0Cu0.5 solder
is to be soldered newly 2455 , 30.3sec.
(preheating : 80~120 for 10~30sec.)
Resistance to Capacitance change : within 7.5% Solder pot : 2705 , 101sec.
Soldering Heat Tan , IR : initial spec.
Vibration Test Capacitance change : within 5% Amplitude : 1.5mm
From 10 to 55 (return : 1min.)
Tan , IR : initial spec.
2hours 3 direction (x, y, z)
Moisture Capacitance change : within 12.5% With rated voltage
Resistance Tan : 0.125 max 402 , 90~95%RH, 500+12/-0hrs
500Mohm or 12.5Mohm
IR :
Whichever is smaller
150%
High Temperature Capacitance change : within 12.5% With of the rated voltage
Resistance Tan : 0.125 max Max. operating temperature
1,000Mohm or 25Mohm
,000+48/-0hrs
IR : 1
Whichever is smaller
Temperature Capacitance change : within 7.5% 1 cycle condition
Cycling Tan , IR : initial spec. Min. operating temperature 25
Max. operating temperature 25
5 cycle test
The reliability test condition can be replaced by the corresponding accelerated test condition.
D. Recommended Soldering method :
Reflow ( Reflow Peak Temperature : 2605 , 30sec. )
Product specifications included in the specifications are effective as of March 1, 2013.
Please be advised that they are standard product specifications for reference only.
We may change, modify or discontinue the product specifications without notice at any time.