884086-000 TE Connectivity

Altera MT5000 Flexible, Modified Polyolefin, Heat - Shrinkable Tubing This specification covers the requirements for one type of single wall, electrical insulating, extruded tubing whose diameter will reduce to a predetermined size upon application of heat in excess of 110C (230F). The tubing is fabricated from modified polyolefin crosslinked by irradiation. It shall be homogenous and essentially free from flaws, defects, pinholes, seams, cracks or inclusions. The tubing is fabricated from materials which meet the requirements of U.S. Pharmacopeia Class VI Plastics. Color shall be black or clear unless otherwise specified. Table 1: Dimensions As Supplied Recovered Inside Diameter Inside Diameter Wall Thickness(Inches, Millimetres) Size Minimum (D) Maximum (d) (W) in. mm. in. mm. Minimum Maximum Nominal 3/64 .046 1.17 .023 0.58 .013 0.33 .019 0.48 .016 0.40 1/16 .063 1.60 .031 0.79 .014 0.35 .020 0.50 .017 0.43 3/32 .093 2.36 .046 1.17 .017 0.43 .023 0.58 .020 0.50 1/8 .125 3.18 .062 1.58 .017 0.43 .023 0.58 .020 0.50 3/16 .187 4.75 .093 2.36 .017 0.43 .023 0.58 .020 0.50 1/4 .250 6.35 .125 3.18 .022 0.56 .028 0.71 .025 0.64 3/8 .375 9.53 .187 4.75 .022 0.56 .028 0.71 .025 0.64 1/2 .500 12.70 .250 6.35 .022 0.56 .028 0.71 .025 0.64 3/4 .750 19.05 .375 9.53 .027 0.69 .033 0.84 .030 0.76 1 1.000 25.40 .500 12.70 .030 0.76 .040 1.01 .035 0.88 1-1/2 1.500 38.10 .750 19.05 .034 0.86 .046 1.17 .040 1.01 2 2.000 50.80 1.000 25.40 .038 0.96 .052 1.32 .045 1.14 Specification Control Drawing TE Connectivity Title: Altera MT5000 300 Constitutional Drive Flexible, Modified Polyolefin, Menlo Park, CA 94025 USA Heat - Shrinkable Tubing TE Connectivity reserves the right to amend this drawing at any Document No : time. Users should evaluate the suitability of the product for their MT5000 application Cage Code: Scale: Size: Rev. Date: Rev.: Sheet: 06090 None A 15-Apr-11 B1 1 of 2 Print Date: 12-May-11 If this document is printed it becomes uncontrolled. Check for the latest revision. Table 2: Properties Property Unit Requirement Test Method Physical Inches (mm) In accordance with Table 1 * Dimensions * Longitudinal Change Percent +0, -10 maximum ASTM D 2671 * Concentricity as supplied Percent 70 minimum ASTM D 2671 * Tensile Strength PSI (MPa) 1800 minimum (12.4) ASTM D 2671, * Ultimate Elongation Percent 200 minimum 20 / minute 4 Secant Modulus PSI (MPa) 2.5 x 10 maximum (172) ASTM D 2671 Heat Resistance 168 hours at 125C (257F) Followed by test for: ASTM D 2671, Ultimate Elongation Percent 100 minimum 20 /minute Electrical Dielectric Strength Volts/mil 500 minimum (19.680) ASTM D 2671 (volts/mm) Dielectric Withstand 3000V, 60 Hz sec 60 minimum ASTM D 2671 Chemical ASTM D 2671 Fluid Resistance 24 hours at 23 3C (77 5F) Isopropyl Alcohol 5% Saline Solution Cidex** Followed by tests for: Dielectric Strength Volts/mil 500 minimum (19,680) ASTM D 2671 (volts/mm) Tensile Strength PSI (MPa) 1800 minimum (12.4) ASTM D 2671 Heavy Metals Analysis ppm 1 maximum USP XXII Cadmium (total of all metals) Physicochemical Mercury Tests-Plastics Lead (Note 1) Bismuth Antimony * Denotes lot acceptance test **Trademark of Johnson & Johnson Company Note 1: Sample preparation and extraction is per USP XXII. Metals analysis may be colorimetric as described in USP XXII or by equivalent quantitative analytical method. Raychem reserves the rights to amend this specification at any time. Users should evaluate the suitability of the product for their application. Rev. Date: Rev.: Document No. Sheet: 15-Apr-11 B1 2 of 2 MT5000 Print Date: 12-May-11 If this document is printed it becomes uncontrolled. Check for the latest revision.