CUSTOMER DRAWING 3mm 1mm Product Dimensions As Received After Free Recovery Maximum Product Weight Name A2.54 B W B W Pounds/mpc (A0.100) min min max min D-300-08 25.40 4.32 0.30 2.03 0.76 1.15 (1.000) (0.170) (0.012) (0.080) (0.030) D-300-12 27.90 6.35 0.38 3.05 1.02 2.55 (1.100) (0.250) (0.015) (0.120) (0.040) D-300-18 33.02 9.14 0.38 4.57 1.27 4.50 (1.300) (0.360) (0.015) (0.180) (0.050) MATERIALS 1. MOLDED CAP: Heat-shrinkable, cross-linked modified polyolefin. 2. MELTABLE RING: Modified thermoplastic. 3. DEFORMABLE DAM: Radiation cross-linked, thermally stabilized modified polyolefin. APPLICATION 1. These parts are designed to meet the requirements as shown in the Requirements Section when tested as listed. 2. Parts to be assembled as outlined herein. 3. B recovered is the maximum inside diameter of the heat-shrinkable cap. 4. W is the wall thickness of the molded cap only, and is measured along the vertical wall. 5. A is the average length of the cap and is equal to (A min + A max)/2. 1.0 SCOPE This document covers the requirements and test procedures applicable to heat shrinkable, stub-splice encapsulation cap (caps) and the molded component thereof. 2.0 APPLICABLE DOCUMENTS The specifications and standards referenced herein shall form part of this specification to the extent specified. Tyco Electronics TITLE: 305 Constitution Dr Menlo Park, CA CAP, SPLICE ENCAPSULATION 94025, U.S.A. DOCUMENT NO.: Unless otherwise specified dimensions are in millimeters. Raychem Inches dimensions are shown in brackets Devices D-300-08/-12/-18 TOLERANCES: ANGLES: N/A Tyco Electronics reserves the right to 0.00 N/A amend this drawing at any time. Users REV: DATE: 0.0 N/A ROUGHNESS should evaluate the suitability of the B 31-July-08 0 N/A IN MICRON product for their application. DRAWN BY: CAGE CODE: REPLACES: ECO NUMBER: SCALE: SIZE: SHEET: M. FORONDA 06090 D010044 08-018889 NTS A 1 of 7 2008 Tyco Electronics Corporation. All rights reserved If this document is printed it becomes uncontrolled. Check for the latest revision. CUSTOMER DRAWING 3.0 REQUIREMENTS 3.1 Material: The splice encapsulation caps shall be fabricated from the materials specified on sheet 1 of this specification. The materials shall be homogenous and essentially free from flaws, defects, pinholes, seams, cracks and inclusions. 3.1.1 Color: The caps shall be black. 3.1.2 Properties of Molded Component: The molded component and the material from which it is fabricated shall meet the requirements in Table 1. 3.1.3 Properties of Finished Caps: The finished caps shall meet the requirements of Table 2. 4.0 QUALITY ASSURANCE PROVISIONS 4.1 Classification of Tests: 4.1.1 Qualification of Tests: Qualification testing shall consist of all test listed in this specification. 4.1.2 Acceptance tests: Acceptance tests shall consist of those tests applicable to Test Groups A and F of Table 2. 4.2 Sampling Instructions: 4.2.1 Qualification Test Samples: Qualification testing shall consist of six molded slabs, 6 x 6 x 0.075 .010 inches and 62 D-300-12 caps. The molded slabs shall be fabricated from the same lot of material and shall be subjected to the same degree of cross-linking as the molded components. 4.2.2 Acceptance Test Samples: Acceptance test samples shall consist of finished caps selected at random in accordance with ANSI/ASQC Z1.4, Inspection Level S-2, AQL 6.5%. A lot of finished caps shall consist of all caps fabricated from the same lot of molded components, from the same production run, and offered for inspection at the same time. 4.3 Test Procedures Molded Slabs 4.3.1 Tensile Strength And Ultimate Elongation: Three specimens cut from a molded slab, using die D of ASTM D 412, shall be tested for tensile strength and ultimate elongation in accordance with ASTM D 412. 4.3.2 Low-Temperature Flexibility: A 6- x inch specimen cut from a molded slab shall be mounted in a loop position between movable, parallel, sets of jaws 2 inches apart, mounted on a test fixture. Each end of the specimen shall extend at least inch into a set of jaws and shall be firmly fastened. The specimen and the test fixture shall be conditioned for four hours at 55 2 C (-67 4 F). While at this temperature, the sets of jaws shall be moved rapidly from a 2 inch to a 1 inch separation. 4.3.3 Heat Shock: Three 6 x inch specimens, cut from a molded slab, shall be conditioned for four hours in a 225 5 C (437 9 F) mechanical-convection oven in which air passes the specimens at a velocity of 100 to 200 feet per minute. After conditioning, the specimens shall be removed from the oven, cooled to room temperature, and visually examined for evidence of dripping, flowing, or cracking. 4.3.4 Heat Aging: 4.3.4.1 Procedure A: Three specimens, prepared and measured in accordance with 4.3.1, shall be conditioned for 168 hours in a 175 5 C (347 9 F) mechanical-convection oven in which air passes the specimens at a velocity of 100 to 200 feet per minute. After conditioning, the specimens shall be removed from the oven, cooled to room temperature, and tested for tensile strength and ultimate elongation in accordance with 4.3.1. Tyco Electronics TITLE: 305 Constitution Dr Menlo Park, CA CAP, SPLICE ENCAPSULATION 94025, U.S.A. DOCUMENT NO.: Unless otherwise specified dimensions are in millimeters. Raychem Inches dimensions are shown in brackets Devices D-300-08/-12/-18 TOLERANCES: ANGLES: N/A Tyco Electronics reserves the right to 0.00 N/A amend this drawing at any time. Users REV: DATE: 0.0 N/A ROUGHNESS should evaluate the suitability of the B 31-July-08 0 N/A IN MICRON product for their application. DRAWN BY: CAGE CODE: REPLACES: ECO NUMBER: SCALE: SIZE: SHEET: M. FORONDA 06090 D010044 08-018889 NTS A 2 of 7 2008 Tyco Electronics Corporation. All rights reserved If this document is printed it becomes uncontrolled. Check for the latest revision.