DWFR Highly Flame-Retardant, Dual Wall Polyolefin Heat-Shrinkable Tubing Adhesive W Expanded As Supplied D Fully Recovered After Heating d Table 1: Dimensions: mm (in) Shrink Size Minimum Maximum Total Minimum Inner Ratio Inside Diameter as Inside Diameter Wall Thickness Meltable Wall supplied (D) after recovery (d) after recovery (W) Thickness after recovery mm (in) mm (in) mm (in) mm (in) 3:1 3/1 3.0 (0.118) 1.0 (0.039) 1.12 0.25 (.044 .010) 0.25 (0.010) 6/2 6.0 (0.236) 2.0 (0.079) 1.14 0.25 (.045 .010) 0.25 (0.010) 9/3 9.0 (0.354) 3.0 (0.118) 1.40 0.25 (.055 .010) 0.56 (0.022) 12/4 12.0 (0.472) 4.0 (0.157) 1.78 0.36 (.070 .014) 0.58 (0.023) 19/6 19.0 (0.748) 6.0 (0.236) 2.25 0.50 (.088 .020) 0.58 (0.023) 24/8 24.0 (0.945) 8.0 (0.315) 2.54 0.50 (.100 .020) 0.79 (0.031) 40/13 40.0 (1.575) 13.0 (0.512) 2.54 0.50 (.100 .020) 0.86 (0.034) 4:1 4/1 4.0 (0.157) 1.0 (0.039) 1.12 0.25 (.044 .010) 0.25 (0.010) 8/2 8.0 (0.315) 2.0 (0.079) 1.14 0.25 (.045 .010) 0.25 (0.010) 12/3 12.0 (0.472) 3.0 (0.118) 1.40 0.25 (.055 .010) 0.56 (0.022) 16/4 16.0 (0.630) 4.0 (0.157) 1.78 0.36 (.070 .014) 0.58 (0.023) 24/6 24.0 (0.945) 6.0 (0.236) 2.25 0.50 (.088 .020) 0.58 (0.023) 32/8 32.0 (1.260) 8.0 (0.315) 2.54 0.50 (.100 .020) 0.79 (0.031) 52/13 52.0 (2.047) 13.0 (0.512) 2.54 0.50 (.100 .020) 0.86 (0.034) Material: The tubing shall be fabricated from a modified irradiated polyolefin compounded to produce a homogeneous, uniform product whose outside surface is essentially free from flaws, defects, pinholes, seams, cracks, or inclusions. The interior wall is coated with a thermoplastic adhesive. The standard color is black. 2016 Tyco Electronics Corporation. All Rights Reserved Customer Drawing Title: Tubing DWFR TE CONNECTIVITY Highly Flame-Retardant, Dual Wall Polyolefin 300 Constitution Drive Menlo Park, CA 94025 USA Heat-Shrinkable Tubing TE Connectivity reserves the right to amend this Document No : drawing at any time. Users should evaluate the DWFR suitability of the product for their application Cage Code: Scale: Size: Rev. Date: Sheet: Rev. E 06090 None A 28-January-16 1 of 2 If this document is printed it becomes uncontrolled. Check for the latest revision. Properties: PROPERTY UNIT REQUIREMENT TEST METHOD PHYSICAL *Dimensions mm (in) In accordance with Table 1 ASTM D 2671 Longitudinal Change Percent 0, -15% ASTM D 2671 *Tensile Strength psi (MPa) 1500 minimum (10.3) ASTM D 2671 *Ultimate Elongation Percent 200 minimum Secant Modulus (Expanded) psi (MPa) 4 ASTM D 882, 2% strain 2.5 x 10 maximum (172) Cold Bend Test --- No cracking UL 224, section 5.9 at -30 1.0C (-22 1.8F) for 1 hour *Heat Shock --- No dripping, flowing or UL 224, section 5.8 4 hours at 250.0 1.0C (482 cracking of outer wall 1.8F) Heat Resistance UL 224 168 hours at 158.0C 1.0C (316.4 1.8F) Followed by test for: - Tensile Strength psi (MPa) Min. 70% of original - Elongation Percent 100% minimum Sealing Efficiency No openings on reheat AMS-DTL 23053/4 ELECTRICAL Dielectric Strength Volts/mil 300 minimum (11,811 min) ASTM D 2671 (volts/mm) on dual wall specimen Volume Resistivity ohm-cm 14 ASTM D 2671 10 minimum on dual wall specimen CHEMICAL Corrosion of the bare copper --- No pitting or blackening of UL 224, section 5.16 168 hours at 158.0C 1.0C (316.4 copper 1.8F) Copper stability --- Show no sign of degradation UL 224, section 5.17 168 hours at 158.0C 1.0C (316.4 1.8F) Followed by test for: - Elongation Percent 100% minimum Flammability Self-extinguishing within 1 --- minute, 25% maximum flag UL 224, VW-1 burn and 0% cotton burn Water Absorption Percent 0.5 maximum ASTM D 2671 24 hours at 23C (73F) * Denotes Lot Acceptance Test Customer Drawing Rev.: Document No. Sheet: Rev. Date: E 28-January-16 2 of 2 DWFR If this document is printed it becomes uncontrolled. Check for the latest revision