QS1500-NO.2-F6-0-45MM TE Connectivity

QS1500 Polyolefin, Flexible, Adhesive Lined, Heat - Shrinkable Tubing Table 1: Dimensions As Supplied As Recovered Minimum Maximum Minimum Minimum Minimum Size Expanded I.D. Recovered Recovered Recovered Recovered Including I.D. Including Jacket Wall Adhesive Total Wall Core (D) Core (d) (W2) Wall (W1) (W) in. mm. in. mm. in. mm. in. mm. in. mm. No. 1 0.225 5.72 0.050 1.27 0.025 0.64 0.022 0.56 0.047 1.20 No. 2 0.300 7.62 0.065 1.65 0.030 0.76 0.030 0.76 0.060 1.52 No. 3 0.455 11.55 0.095 2.41 0.035 0.89 0.040 1.02 0.075 1.91 No. 4 0.700 17.78 0.175 4.45 0.041 1.04 0.054 1.37 0.095 2.41 No. 5 1.100 27.94 0.300 7.62 0.076 1.93 0.062 1.57 0.138 3.51 Material: Fabricated from flame-retarded crosslinked modified flexible polyolefin, with a thermoplastic adhesive liner. Color: Jacket shall be black. Adhesive liner shall be amber. Table 2: Properties: Property Unit Requirement Test Method Specific Gravity -- 1.35 maximum ASTM D 792 Note 1 Dimensions Inches Table 1 ASTM D 2671 Longitudinal Change Percent 0 to -10 ASTM D 2671 Tensile Strength PSI 1300 minimum ASTM D 2671 Speed 2 in./min. Note 2 Ultimate Elongation Percent 200 minimum ASTM D 2671 Speed 2 in./min. Low Temperature Flexibility -- No Cracking ASTM D 2671 -40C Heat Shock -- No Cracking ASTM D 2671 4 hrs. at 250C CUSTOMER DRAWING Tyco Electronics Corporation Raychem Title: QS1500 300 Constitutional Drive Tubing Polyolefin, Flexible, Adhesive Lined, Menlo Park, CA 94025 USA Heat - Shrinkable Tubing Tyco Electronics reserves the right to amend this drawing at any time. Document No : Users should evaluate the suitability of the product for their application QS1500 Cage Code: Scale: Size: Rev. Date: Rev.: Sheet: 06090 None A 5-Jan-10 C 1 of 2 2010 Tyco Electronics Corporation. All rights reserved. If this document is printed it becomes uncontrolled. Check for the latest revision. Properties, continued Property Unit Requirement Test Method Heat Aging, -- No Cracking Note 3 168 hrs at 175C Dielectric Strength, (jacket only)* Volts/mil 350 minimum ASTM D 149 12 Volume Resistivity ohm-cm 10 minimum ASTM D 257 Flammability -- Self extinguishing in 1 minute ASTM D 2671 Procedure B Mandrel size 50% of Expanded I.D. Water Absorption Percent 1.0 maximum ASTM D 570, Procedure A * Adhesive liner manually removed prior to testing. Qualification Sizes: QS1500-1 qualifies QS1500-1 and QS1500-2 QS1500-3 qualifies QS1500-3 and QS1500-5 Note 1: Sample Preparation Unless otherwise specified, all tests will be performed on tubing specimens which have been recovered by conditioning for 10 minutes in a 150C air circulating oven and then allowed to stabilize at 233C for 3 hours. Note 2: Tensile Strength Calculate Tensile Strength based on wall thickness of jacket only. Note 3: Thermal Aging Three samples shall be conditioned for 168 hours in an air circulating oven at 1753C. After conditioning, the specimens shall be cooled to room temperature and bent through 180 over a mandrel selected in accordance to Table 3. Any side cracking caused by flattening of the specimen on the mandrel shall be disregarded. Table 3: Mandrel Sizes Tube SizeI.D, inches Mandrel, O.D. inches .047 ID .250 .313 .250 ID .500 .375 .500 ID 2.0 .437 Acceptance tests shall consist of: Dimensions Longitudinal Change Acceptance tests shall be performed on each lot of tubing or on a skip-lot basis per a statistically justified control plan determined by Tyco Electronics. CUSTOMER DRAWING Rev.: Document No. Sheet: Rev. Date: C 2 of 2 5-Jan-10 QS1500 If this document is printed it becomes uncontrolled. Check for the latest revision.