SCT Splice Cover (Dual Wall) Heat-Shrinkable Tubing Table 1: Dimensions (mm/inches) As Supplied As Recovered Size Minimum Maximum Recovered Total Minimum Recovered Expanded I.D. Recovered I.D. Wall Adhesive Wall (D) (d) (W) (W1) No.1 7.62 (0.300) 1.65 (0.065) 1.52 (0.060) 0.30 (0.012) 0.76 (0.030) No.2 9.02 (0.355) 2.29 (0.090) 1.52 (0.060 ) 0.30 (0.012) 0.76 (0.030) No.3 11.56 (0.455) 2.54 (0.100) 2.29 (0.090) 0.30 (0.012) 1.40 (0.055) No.4 17.78 (0.700) 4.45 (0.175) 2.54 (0.100) 0.30 (0.012) 1.52 (0.060) No.5 27.94 (1.100) 8.38 (0.330) 2.54 (0.100) 0.30 (0.012) 1.52 (0.060) Color: Jacket shall be black adhesive liner shall be amber. Marking is SCT-1, SCT-2, SCT-3, SCT-4, SCT-5 2000,2011 Tyco Electronics Corporation, a TE Connectivity Ltd. Company. All Rights Reserved. Customer Drawing TE Connectivity Raychem Title: SCT 305 Constitution Drive Tubing Splice Cover Dual Wall Menlo Park, CA 94025 USA Heat-Shrinkable Tubing TE Connectivity reserves the right to amend this drawing at any Document No : time. Users should evaluate the suitability of the product for their SCT application Cage Code: Scale: Size: Rev. Date: Rev.: Sheet: 06090 None A 15-Apr-11 J1 1 of 3 Print Date: 18-Apr-11 If this document is printed it becomes uncontrolled. Check for the latest revision. Table 2: Properties Property Unit Requirements Test Method Dimensions Inches Table 1 ASTM D 2671 Tensile Strength PSI 1500 minimum ASTM D 2671 Ultimate Elongation Percent 300 minimum ASTM D 2671 Speed 2 in./min. Note 1 Secant Modulus PSI 35000 minimum ASTM D 2671 (Expanded Tubing) Speed 2 in./min. Longitudinal Change Percent +0 to -10 ASTM D 2671 Note 1 Concentricity Percent 60 minimum ASTM D 2671 (Expanded Form) Dielectric Strength* Volts/mil 500 minimum ASTM D 149 (Jacket Only) 13 Volume Resistivity Ohm-cm 10 minimum ASTM D 257 Immersion Leak Resistance Micro-amps 0.25 maximum Note 2 Thermal Cycling Micro-amps 0.25 maximum Note 3 25 cycles -40C to 135C, followed by: Immersion Leak Resistance, Note 2. Heat Shock -- No dripping, flowing or ASTM D 2671 4 hrs 250C cracking of jacket Thermal Aging Micro-amps 0.25 maximum Note 4 1000 hrs 150C, followed by: Immersion Leak Resistance, Note 2. Fluid Resistance Micro-amps 0.25 maximum Note 5 24 hrs. 25 3C ASTM Reference Fuel C VV-F-800 Diesel Fuel 24 hrs 100 3C ASTM 3 Oil Followed by: Immersion Leak Resistance, Note 2. Qualification Sizes: SCT-2 qualifies SCT-1, SCT-2 and SCT-3 SCT-4 qualifies SCT-4 and SCT-5 Note 1: Tensile Strength & Secant Modulus Calculate Tensile Strength and Secant Modulus based on wall thickness of jacket only Customer Drawing Rev.: Document No. Sheet: Rev. Date: J1 2 of 3 15-Apr-11 SCT Print Date: 18-Apr-11 If this document is printed it becomes uncontrolled. Check for the latest revision.