ELASTOSIL N10 RTV-1 SILICONE RUBBER / ADHESIVE AND SEALANT Product description Afterwards only the use of mechanical forces in combination with a swelling solvent or the use of high ELASTOSIL N10 is a flowable silicone sealant which temperatures of approximately 100 C will help to cures at room temperature under influence of remove sealant residues. ELASTOSIL N10 shows atmospheric moisture. good primerless adhesion to many substrates. We recommend to run preliminary tests to optimize Special features conditions for the particular application. - neutral-curing system (oxime) Storage - low viscosity, no thixotropy - solventfree The Best use before end date of each batch is shown - excellent primerless adhesion to many substrates on the product label. Storage beyond the date specified on the label does Application not necessarily mean that the product is no longer usable. In this case however, the properties required Multipurpose grade for bonding, sealing and potting for the intended use must be checked for quality e.g in electronic applications. assurance reasons. Safety notes Processing During vulcanization of ELASTOSIL N10, a total of ELASTOSIL N10 is a one-part room temperature 4% by weight of an oxime is being split off. These vulcanizing sealant that cures to a flexible silicone vapours should not be inhaled for long periods or in rubber on exposure to atmospheric moisture. Higher high concentration. Work areas should therefore be humidity accelerates skin formation and curing as well well ventilated. Contact of unvulcanized silicone rubber as elevated temperature. However temperature shall with eyes and mucous membranes must be avoided as not exceed 50C during cure. During the crosslinking this would cause irritation. However if it does happen, process, some oxime by-product is released. After rinse the affected area thoroughly with water. about 25 minutes a dry skin is formed. After formation Comprehensive instructions are given in the of a sufficiently thick skin, glued parts may be handled corresponding Material Safety Data Sheets. They are without destruction. If removing of silicone rubber from available on request from WACKER subsidiaries or machines or dispensing equipment is necessary, white may be printed via WACKER web site spirit is recommended as a solvent. However, cleaning Product data Typical general characteristics Inspection Method Value Product data (uncured) Color colorless Density at 23 C 1,01 g/cm Viscosity, dynamic at 23 C BROOKFIELD 8000 mPa.s Skin-forming time, 23 C, 50 % RH 25 min Product data (cured) Density ISO 2781 1,02 g/cm Hardness Shore A ISO 868 25 Elongation at break ISO 37 200 % 2 Tensile strength ISO 37 1,50 N/mm Tear strength ASTM D 624 B 3,0 N/mm 2 mm, 14 d storage at 20 C, 50 % RH These figures are only intended as a guide and should not be used in preparing specifications. The management system has been The data presented in this leaflet are in accordance with the present state of For technical, quality, or product certified according to DIN EN ISO our knowledge, but do not absolve the user from carefully checking all safety questions, please contact: 9001 and DIN EN ISO 14001 supplies immediately on receipt. We reserve the right to alter product constants within the scope of technical progress or new developments. The Wacker Chemie AG WACKER is a trademark of Wacker recommendations made in this leaflet should be checked by preliminary Hanns-Seidel-Platz 4 Chemie AG. trials because of conditions during processing over which we have no 81737 Mnchen, Germany ELASTOSIL is a trademark of control, especially where other companies raw materials are also being info.silicones wacker.com Wacker Chemie AG. used. The recommendations do not absolve the user from the obligation of investigating the possibility of infringement of third parties rights and, if www.wacker.com necessary, clarifying the position. Recommendations for use do not constitute a warranty, either express or implied, of the fitness or suitability of the products for a particular purpose. Technical data sheet for ELASTOSIL N10 / Version: 1.1 / Date of last alteration: 07.06.2013 2 / 2