SIL-PAD 400 The Original Fiberglass Based Sil-Pad SIL-PAD 400 Sil-Pad 400 is the original Sil-Pad material. Sil-Pad 400 is a composite of silicone rubber and berglass. It is ame retardant and is specially formulated for use as a thermally conductive insulator. Primary use is to electrically isolate power sources from heat sinks. Sil-Pad 400 has excellent mechanical and physical characteristics. Surfaces are pliable and allow complete surface contact with excellent heat dissipation. Sil-Pad 400 actually improves its thermal resistance with age. The reinforcing berglass gives excellent cut-through resistance and Sil-Pad 400 is non-toxic and resists damage from cleaning agents. SIL-PAD 600 Special Thicknesses, Rolls and Sheets Sil-Pad 600 is a silicone elastomer lled with special Sil-Pad 400 can be supplied on special order in a variety ingredients to provide higher thermal performance. This of thicknesses from .007 to .045 inches to fulll special material has similar physical characteristics of the Sil-Pad requirements of insulation path minimums or other spacing 400 material with enhanced thermal performance. needs. Sil-Pad 400 and 600 are available in die-cut parts, sheets (6 x 6 min., 6 x 12 , 8 x 8 , 10 x 10 and 12 x 12 ) and roll form. Physical Properties Sil-Pad 400, .007 in. Sil-Pad 400, .009 in Sil-Pad 600 Test Method Color Gray Gray Green Thickness Inches .007 .001 .009 .001 .009 .001 (mm) 0.178 0.025 .229 .025 .229 .025 ASTM D 374 Breaking Strength Lbs/inch (kN/m) 100 (18) 100 (18) 100 (18) ASTM D 1458 Elongation, % 45 to warp and ll 40 40 40 ASTM D 412 Hardness, Shore A 85 85 85 ASTM D 2240 Tensile Strength, kPsi (MPa) 45 to warp and ll 3 (20) 3 (20) ASTM D 412 Continuous Use Temp., C -60 to +180 -60 to +180 -60 to +180 Specic Gravity 2.0 2.0 1.8 ASTM D 792 Construction Silicone/Fiberglass Silicone/ Fiberglass Thermal Vacuum Weight Loss % (TML) as manufactured .40 .40 NASA Post Cure 24 Hrs. 400 F .25 .25 SP-R-0022A Volatile Condensable Material % (CVCM) as manufactured .11 .11 NASA Post Cure 24 Hrs. 400F .07 .07 SP-R-0022A Thermal Properties Sil-Pad 400, .007 in. Sil-Pad 400, .009 in Sil-Pad 600 Test Method 2 Thermal Resistance, C-in /W 0.45 0.50 0.35 ASTM D 5470 Thermal Conductivity, W/m-K 0.9 0.9 1.0 ASTM D 5470 Electrical Properties Sil-Pad 400, .007 in. Sil-Pad 400, .009 in Sil-Pad 600 Test Method Breakdown Voltage, Volts a-c Min. 3500 4500 4500 ASTM D 149 Dielectric Constant, 1000 Cps (Hz) 5.5 5.5 5.0 ASTM D 150 11 11 11 Volume Resistivity, Ohm Metre 1.0 x 10 1.0 x 10 1.0 x 10 ASTM D 257 25X-ON Electronics Largest Supplier of Electrical and Electronic Components Click to view similar products for bergquist company manufacturer: Other Similar products are found below : SIL-PAD 2000 150MMX150MM SHEET GPEMI1.0-0.060-01-0816 SPA2000-0.020-00-1012 SPK6-0.006-AC-11.512 TGP6000ULM- 0.125-12-0816 803265 GPEMI1.0-0.040-01-0816 GP3500ULM-G-0.100-12-0816 TGP12000ULM-0.080-00-0808 GP1500-0.160-02-0816 TGP3000ULM-0.080-02-0816 SIL-PAD K6 300MMX300MM SHEET GP1500-0.200-02-0816 SP980-0.009-00-1212 GPEMI1.0- 0.100-01-0816 GPA3000-0.125-01-0816 TGP12000ULM-0.100-00-0808 TGP12000ULM-0.060-00-0808 TGP3000ULM-0.120-02-0816 803263 GP1000SF-0.100-02-0816 GPHC1000-0.010-02-0816 GP1500S30-0.100-02-0816 LF2000-00-00-30CC TGP3000ULM- 0.100-02-0816 TGP12000ULM-0.125-00-0808 803269 2015-54 GPVOUS-0.080-00-4/4 SP1200-0.016-AC-1212 SPA1500-0.010-00-4/4 GP1500S30-0.250-02-0816 SPA2000-0.015-AC-1012 GP3500ULM-G-0.080-12-0816 GPVO-0.160-01-0816 GP1500S30-0.125-02-0816 BP660P-0.008-00-1112 LF3800LVO-00-150CC 803790 803266 BP100-0.005-00-1/1 SP1200-0.012-AC-1212 SP1500ST-0.012-02-1012 HF625-0.005-AC-1212 GF2000-00-600-50CC GPVOUS-0.160-AC-0816 GPVOUS-B-0.040-01-0816 803262 803268 SPA2000- 0.015-00-1012