04026D100JAT2A Kyocera AVX

X5R Dielectric General Specifications GENERAL DESCRIPTION General Purpose Dielectric for Ceramic Capacitors EIA Class II Dielectric Temperature variation of capacitance is within 15% from -55C to +85C Well suited for decoupling and filtering applications Available in High Capacitance values (up to 100F) PART NUMBER (SEE PAGE 4 FOR COMPLETE PART NUMBER EXPLANATION) 1210 4 D 107 M A T 2 A Size Voltage Dielectric Capacitance Capacitance Failure Terminations Packaging Special (L x W) 4 = 4V D = X5R Code (In pF) Tolerance Rate T = Plated Ni 2 = 7 Reel Code 0101** 6 = 6.3V 2 Sig. Digits + K = 10% A = N/A and Sn 4 = 13 Reel A = Std. 0201 Z = 10V Number of M = 20% U = 4mm TR 0402 Y = 16V Zeros (01005) 0603 3 = 25V 0805 D = 35V 1206 5 = 50V 1210 1 = 100V 1812 **EIA 01005 NOTE: Contact factor y for availability of Tolerance Options for Specific Par t Numbers. Contact factor y for non-specified capacitance values. TYPICAL ELECTRICAL CHARACTERISTICS Insulation Resistance vs Temperature 10,000 20 15 10 1,000 0 -5 -10 100 -15 -20 0 -60 -40 -20 0 +20 +40 +60 +80 20 40 60 80 100 120 Temperature C Temperature C The Important Information/Disclaimer is incorporated in these specifications by reference and should be reviewed in full before placing any order. 25 121818 % Capacitance Insulation Resistance (Ohm-Farads) X5R Dielectric Specifications and Test Methods Parameter/Test X5R Specification Limits Measuring Conditions Operating Temperature Range -55C to +85C Temperature Cycle Chamber Capacitance Within specified tolerance 2.5% for 50V DC rating Freq.: 1.0 kHz 10% 12.5% for 25V, 35V DC rating Voltage: 1.0Vrms .2V Dissipation Factor 12.5% Max. for 16V DC rating and lower For Cap > 10 F, 0.5Vrms 120Hz Contact Factor y for DF by PN 10,000M or 500M - F, Charge device with rated voltage for 120 5 Insulation Resistance whichever is less secs room temp/humidity Charge device with 250% of rated voltage for Dielectric Strength No breakdown or visual defects 1-5 seconds, w/charge and discharge current limited to 50 mA (max) Appearance No defects Deflection: 2mm Capacitance Test Time: 30 seconds 12% Variation Resistance to Flexure Dissipation Meets Initial Values (As Above) Stresses Factor Insulation Initial Value x 0.3 Resistance 95% of each terminal should be covered with Dip device in eutectic solder at 230 5C for 5.0 Solderability fresh solder 0.5 seconds Appearance No defects, <25% leaching of either end terminal Capacitance 7.5% Variation Dissipation Dip device in eutectic solder at 260C for Resistance to Meets Initial Values (As Above) Factor 60seconds. Store at room temperature for 24 Solder Heat 2hours before measuring electrical properties. Insulation Meets Initial Values (As Above) Resistance Dielectric Meets Initial Values (As Above) Strength Appearance No visual defects Step 1: -55C 2 30 3 minutes Capacitance 7.5% Step 2: Room Temp 3 minutes Variation Dissipation Meets Initial Values (As Above) Step 3: +85C 2 30 3 minutes Thermal Shock Factor Insulation Meets Initial Values (As Above) Step 4: Room Temp 3 minutes Resistance Dielectric Repeat for 5 cycles and measure after 24 2 Meets Initial Values (As Above) Strength hours at room temperature Appearance No visual defects Charge device with 1.5X rated voltage in test Capacitance chamber set at 85C 2C for 1000 hours 12.5% Variation (+48, -0). Dissipation Initial Value x 2.0 (See Above) Note: Contact factor y for *optional specification Factor Load Life par t numbers that are tested at < 1.5X rated Insulation voltage. Initial Value x 0.3 (See Above) Resistance Remove from test chamber and stabilize at Dielectric Meets Initial Values (As Above) room temperature for 24 2 hours Strength Appearance No visual defects Capacitance 12.5% Store in a test chamber set at 85C 2C/ 85% Variation 5% relative humidity for 1000 hours (+48, -0) Dissipation with rated voltage applied. Initial Value x 2.0 (See Above) Load Factor Humidity Remove from chamber and stabilize at room Insulation Initial Value x 0.3 (See Above) temperature and humidity for Resistance 24 2 hours before measuring. Dielectric Meets Initial Values (As Above) Strength The Important Information/Disclaimer is incorporated in these specifications by reference and should be reviewed in full before placing any order. 26 042418