LD025A560FAB2A\500 Kyocera AVX

MLCC Tin/Lead Termination B C0G (NP0) General Specifications AVX Corporation will support those customers for commercial and military Multilayer Ceramic Capacitors with a termination consisting of 5% minimum lead. This termination is indicated by the use of a B in the 12th position of the AVX Catalog Part Number. This fulfills AVXs commitment to providing a full range of products to our customers. AVX has provided in the following pages a full range of values that we are currently offering in this special B termination. Please contact the factory if you require additional information on our MLCC Tin/Lead Termination B products. Not RoHS Compliant PART NUMBER (see page 2 for complete part number explanation) LD05 A 101 J A B 5 2 A Size Dielectric Capacitance Capacitance Failure Terminations Voltage Packaging Special LD02 - 0402 C0G (NP0) = A Code (In pF) Tolerance Rate 6.3V = 6 B = 5% min lead 2 = 7 Reel Code LD03 - 0603 X7R = C B = .10 pF (<10pF) A = Not 10V = Z 2 Sig. Digits + 4 = 13 Reel A = Std. X = FLEXITERM LD04 - 0504* X5R = D C = .25 pF (<10pF) Applicable 16V = Y Product Number of with 5% min LD05 - 0805 X8R = F D = .50 pF (<10pF) 25V = 3 Contact Factory Zeros lead** LD06 - 1206 F = 1% ( 10 pF) 35V = D For LD10 - 1210 G = 2% ( 10 pF) 50V = 5 Multiples **X7R only LD12 - 1812 J = 5% 100V = 1 LD13 - 1825 K = 10% 200V = 2 LD14 - 2225 M = 20% 500V = 7 LD20 - 2220 See FLEXITERM section for CV options *LD04 has the same CV ranges as LD03. NOTE: Contact factory for availability of Tolerance Options for Specific Part Numbers. Contact factory for non-specified capacitance values. Insulation Resistance vs Temperature 10,000 1,000 100 0 0 20 40 60 80 100 Temperature C 112916 40 Insulation Resistance (Ohm-Farads)MLCC Tin/Lead Termination B C0G (NP0) Specifications and Test Methods Parameter/Test NP0 Specification Limits Measuring Conditions Operating Temperature Range -55C to +125C Temperature Cycle Chamber Capacitance Within specified tolerance Freq.: 1.0 MHz 10% for cap 1000 pF <30 pF: Q 400+20 x Cap Value 1.0 kHz 10% for cap > 1000 pF Q 30 pF: Q 1000 Voltage: 1.0Vrms .2V 100,000M or 1000M - F, Charge device with rated voltage for Insulation Resistance whichever is less 60 5 secs room temp/humidity Charge device with 250% of rated voltage for Dielectric Strength No breakdown or visual defects 1-5 seconds, w/charge and discharge current limited to 50 mA (max) Note: Charge device with 150% of rated voltage for 500V devices. Appearance No defects Deflection: 2mm Capacitance Test Time: 30 seconds 5% or .5 pF, whichever is greater Resistance to Variation Flexure Q Meets Initial Values (As Above) Stresses Insulation Initial Value x 0.3 Resistance 95% of each terminal should be covered Dip device in eutectic solder at 230 5C Solderability with fresh solder for 5.0 0.5 seconds Appearance No defects, <25% leaching of either end terminal Capacitance 2.5% or .25 pF, whichever is greater Variation Dip device in eutectic solder at 260C for 60 seconds. Store at room temperature for 24 2 Resistance to Q Meets Initial Values (As Above) Solder Heat hours before measuring electrical properties. Insulation Meets Initial Values (As Above) Resistance Dielectric Meets Initial Values (As Above) Strength Appearance No visual defects Step 1: -55C 2 30 3 minutes Capacitance 2.5% or .25 pF, whichever is greater Step 2: Room Temp 3 minutes Variation Thermal Q Meets Initial Values (As Above) Step 3: +125C 2 30 3 minutes Shock Insulation Meets Initial Values (As Above) Step 4: Room Temp 3 minutes Resistance Dielectric Repeat for 5 cycles and measure after Meets Initial Values (As Above) Strength 24 hours at room temperature Appearance No visual defects Capacitance 3.0% or .3 pF, whichever is greater Variation Charge device with twice rated voltage in 30 pF: Q 350 test chamber set at 125C 2C Q Load Life 10 pF, <30 pF: Q 275 +5C/2 for 1000 hours (+48, -0). (C=Nominal Cap) <10 pF: Q 200 +10C Insulation Remove from test chamber and stabilize at Initial Value x 0.3 (See Above) Resistance room temperature for 24 hours Dielectric before measuring. Meets Initial Values (As Above) Strength Appearance No visual defects Capacitance 5.0% or .5 pF, whichever is greater Variation Store in a test chamber set at 85C 2C/ 30 pF: Q 350 85% 5% relative humidity for 1000 hours Load Q 10 pF, <30 pF: Q 275 +5C/2 (+48, -0) with rated voltage applied. Humidity <10 pF: Q 200 +10C Insulation Remove from chamber and stabilize at Initial Value x 0.3 (See Above) Resistance room temperature for 24 2 hours Dielectric before measuring. Meets Initial Values (As Above) Strength 112916 41