MLCC Tin/Lead Termination (LD Series) C0G (NP0) General Specifications AVX Corporation will support those customers for commercial and military Multilayer Ceramic Capacitors with a termination consisting of 5% minimum lead. This termination is indicated by the use of a B in the 12th position of the AVX Catalog Part Number. This fulfills AVXs commitment to providing a full range of products to our customers. AVX has provided in the following pages a full range of values that we are currently offering in this special B termination. Please contact the factory if you require additional information on our MLCC Tin/Lead Termination B products. PART NUMBER (SEE PAGE 4 FOR COMPLETE PART NUMBER EXPLANATION) LD05 5 A 101 J A B 2 A Size Voltage Dielectric Capacitance Failure Terminations Packaging Special Capacitance LD02 - 0402 6.3V = 6 C0G (NP0) = A Code (In pF) Rate B = 5% min lead 2 = 7 Reel Code Tolerance LD03 - 0603 10V = Z X7R = C 2 Sig. Digits + A = Not X = FLEXITERM 4 = 13 Reel A = Std. B = .10 pF (<10pF) LD04 - 0504* 16V = Y X5R = D Number of Applicable with 5% min Product C = .25 pF (<10pF) LD05 - 0805 Contact Factory 25V = 3 X8R = F Zeros lead** D = .50 pF (<10pF) LD06 - 1206 For 35V = D F = 1% ( 10 pF) LD10 - 1210 Multiples* 50V = 5 G = 2% ( 10 pF) **X7R only LD12 - 1812 100V = 1 LD13 - 1825 J = 5% LD14 - 2225 200V = 2 K = 10% LD20 - 2220 500V = 7 M = 20% *LD04 has the same CV ranges as LD03. See FLEXITERM section for CV options NOTE: Contact factory for availability of Tolerance Options for Specific Part Numbers. Contact factory for non-specified capacitance values. Insulation Resistance vs Temperature 10,000 1,000 100 0 0 20 40 60 80 100 Temperature C The Important Information/Disclaimer is incorporated in these specifications by reference and should be reviewed in full before placing any order. 39 112916 Insulation Resistance (Ohm-Farads)MLCC Tin/Lead Termination B C0G (NP0) Specifications and Test Methods Parameter/Test NP0 Specification Limits Measuring Conditions Operating Temperature Range -55C to +125C Temperature Cycle Chamber Capacitance Within specified tolerance Freq.: 1.0 MHz 10% for cap 1000 pF <30 pF: Q 400+20 x Cap Value 1.0 kHz 10% for cap > 1000 pF Q 30 pF: Q 1000 Voltage: 1.0Vrms .2V 100,000M or 1000M - F, Charge device with rated voltage for Insulation Resistance whichever is less 60 5 secs room temp/humidity Charge device with 250% of rated voltage for 1-5 seconds, w/charge and discharge current Dielectric Strength No breakdown or visual defects limited to 50 mA (max) Note: Charge device with 150% of rated voltage for 500V devices. Appearance No defects Deflection: 2mm Test Time: 30 seconds Capacitance 5% or .5 pF, whichever is greater Resistance to Variation Flexure Q Meets Initial Values (As Above) Stresses Insulation Initial Value x 0.3 Resistance 95% of each terminal should be covered Dip device in eutectic solder at 230 5C Solderability with fresh solder for 5.0 0.5 seconds Appearance No defects, <25% leaching of either end terminal Capacitance 2.5% or .25 pF, whichever is greater Variation Dip device in eutectic solder at 260C for 60 Resistance to Q Meets Initial Values (As Above) seconds. Store at room temperature for 24 2 Solder Heat hours before measuring electrical properties. Insulation Meets Initial Values (As Above) Resistance Dielectric Meets Initial Values (As Above) Strength Appearance No visual defects Step 1: -55C 2 30 3 minutes Capacitance 2.5% or .25 pF, whichever is greater Step 2: Room Temp 3 minutes Variation Q Meets Initial Values (As Above) Step 3: +125C 2 30 3 minutes Thermal Shock Insulation Meets Initial Values (As Above) Step 4: Room Temp 3 minutes Resistance Dielectric Repeat for 5 cycles and measure after Meets Initial Values (As Above) Strength 24 hours at room temperature Appearance No visual defects Capacitance 3.0% or .3 pF, whichever is greater Variation Charge device with twice rated voltage in test chamber set at 125C 2C 30 pF: Q 350 for 1000 hours (+48, -0). Q 10 pF, <30 pF: Q 275 +5C/2 Load Life <10 pF: Q 200 +10C Remove from test chamber and stabilize at room Insulation temperature for 24 hours Initial Value x 0.3 (See Above) Resistance before measuring. Dielectric Meets Initial Values (As Above) Strength Appearance No visual defects Capacitance 5.0% or .5 pF, whichever is greater Variation Store in a test chamber set at 85C 2C/ 85% 30 pF: Q 350 5% relative humidity for 1000 hours Q 10 pF, <30 pF: Q 275 +5C/2 (+48, -0) with rated voltage applied. Load <10 pF: Q 200 +10C Humidity Remove from chamber and stabilize at room Insulation Initial Value x 0.3 (See Above) temperature for 24 2 hours before measuring. Resistance Dielectric Meets Initial Values (As Above) Strength The Important Information/Disclaimer is incorporated in these specifications by reference and should be reviewed in full before placing any order. 40 112916