MLCC Tin/Lead Termination (LD Series)
C0G (NP0) General Specifications
AVX Corporation will support those customers for commercial and military Multilayer Ceramic Capacitors with a
termination consisting of 5% minimum lead. This termination is indicated by the use of a B in the 12th position
of the AVX Catalog Part Number. This fulfills AVXs commitment to providing a full range of products to our
customers. AVX has provided in the following pages a full range of values that we are currently offering in this
special B termination. Please contact the factory if you require additional information on our MLCC Tin/Lead
Termination B products.
PART NUMBER (SEE PAGE 4 FOR COMPLETE PART NUMBER EXPLANATION)
LD05 5 A 101 J A B 2 A
Size Voltage Dielectric Capacitance Failure Terminations Packaging Special
Capacitance
LD02 - 0402
6.3V = 6 C0G (NP0) = A Code (In pF) Rate B = 5% min lead 2 = 7" Reel Code
Tolerance
LD03 - 0603
10V = Z X7R = C 2 Sig. Digits + A = Not X = FLEXITERM 4 = 13" Reel A = Std.
B = .10 pF (<10pF)
LD04 - 0504*
16V = Y X5R = D Number of Applicable with 5% min Product
C = .25 pF (<10pF)
LD05 - 0805 Contact Factory
25V = 3 X8R = F Zeros 4 = Automotive lead**
D = .50 pF (<10pF)
LD06 - 1206
For
35V = D
F = 1% ( 10 pF)
LD10 - 1210
Multiples*
50V = 5
G = 2% ( 10 pF) **X7R only
LD12 - 1812
100V = 1
LD13 - 1825 J = 5%
LD14 - 2225 200V = 2
K = 10%
LD20 - 2220
500V = 7
M = 20%
*LD04 has the same CV ranges as LD03. See FLEXITERM section for CV options
NOTE: Contact factory for availability of Tolerance Options for Specific Part Numbers.
Contact factory for non-specified capacitance values.
Insulation Resistance vs Temperature
10,000
1,000
100
0
0 20 40 60 80 100
Temperature C
The Important Information/Disclaimer is incorporated in the catalog where these specifications came from or
available online at www.avx.com/disclaimer/ by reference and should be reviewed in full before placing any order.
39
042320
Insulation Resistance (Ohm-Farads)MLCC Tin/Lead Termination B
C0G (NP0) Specifications and Test Methods
Parameter/Test NP0 Specification Limits Measuring Conditions
Operating Temperature Range -55C to +125C Temperature Cycle Chamber
Capacitance Within specified tolerance
Freq.: 1.0 MHz 10% for cap 1000 pF
1.0 kHz 10% for cap > 1000 pF
<30 pF: Q 400+20 x Cap Value
Q
Voltage: 1.0Vrms .2V
30 pF: Q 1000
100,000M or 1000M - F, Charge device with rated voltage for
Insulation Resistance
whichever is less 60 5 secs @ room temp/humidity
Charge device with 250% of rated voltage for
1-5 seconds, w/charge and discharge current
Dielectric Strength No breakdown or visual defects limited to 50 mA (max)
Note: Charge device with 150% of rated voltage
for 500V devices.
Appearance No defects
Deflection: 2mm
Test Time: 30 seconds
Capacitance
5% or .5 pF, whichever is greater
Resistance to
Variation
Flexure
Q Meets Initial Values (As Above)
Stresses
Insulation
Initial Value x 0.3
Resistance
95% of each terminal should be covered Dip device in eutectic solder at 230 5C
Solderability
with fresh solder for 5.0 0.5 seconds
Appearance No defects, <25% leaching of either end terminal
Capacitance
2.5% or .25 pF, whichever is greater
Variation
Dip device in eutectic solder at 260C for 60
Resistance to
Q Meets Initial Values (As Above)
seconds. Store at room temperature for 24 2
Solder Heat
hours before measuring electrical properties.
Insulation
Meets Initial Values (As Above)
Resistance
Dielectric
Meets Initial Values (As Above)
Strength
Appearance No visual defects Step 1: -55C 2 30 3 minutes
Capacitance
2.5% or .25 pF, whichever is greater Step 2: Room Temp 3 minutes
Variation
Q Meets Initial Values (As Above) Step 3: +125C 2 30 3 minutes
Thermal Shock
Insulation
Meets Initial Values (As Above) Step 4: Room Temp 3 minutes
Resistance
Dielectric Repeat for 5 cycles and measure after
Meets Initial Values (As Above)
Strength 24 hours at room temperature
Appearance No visual defects
Capacitance
3.0% or .3 pF, whichever is greater
Variation Charge device with twice rated voltage in test
chamber set at 125C 2C
30 pF: Q 350
for 1000 hours (+48, -0).
Q 10 pF, <30 pF: Q 275 +5C/2
Load Life
<10 pF: Q 200 +10C
Remove from test chamber and stabilize at room
Insulation temperature for 24 hours
Initial Value x 0.3 (See Above)
Resistance before measuring.
Dielectric
Meets Initial Values (As Above)
Strength
Appearance No visual defects
Capacitance
5.0% or .5 pF, whichever is greater
Variation
Store in a test chamber set at 85C 2C/ 85%
30 pF: Q 350
5% relative humidity for 1000 hours
Q 10 pF, <30 pF: Q 275 +5C/2
Load (+48, -0) with rated voltage applied.
<10 pF: Q 200 +10C
Humidity
Remove from chamber and stabilize at room
Insulation
Initial Value x 0.3 (See Above)
temperature for 24 2 hours before measuring.
Resistance
Dielectric
Meets Initial Values (As Above)
Strength
The Important Information/Disclaimer is incorporated in the catalog where these specifications came from or
available online at www.avx.com/disclaimer/ by reference and should be reviewed in full before placing any order.
40
112916