Reference Only Spec.No.JENF243A-9137B-01 P1/8 Chip Ferrite Bead BLM15HBH1D Murata Standard Reference Specification AEC-Q200 1.Scope This reference specification applies to Chip Ferrite Bead BLM15H BH series for Automotive Electronics based on AEC-Q200. 2.Part Numbering (ex.) BL M 15 HG 102 B H 1 D (1) (2) (3) (4) (5) (6) (7) (8) (9) (1)Product ID (4)Characteristics (7)Category(for Automotive Electronics) (2)Type (5)Typical Impedance at 100MHz (8)Numbers of Circuit (3)Dimension (LW) (6)Performance (9)Packaging (D:Taping) 3.Rating Rated Current DC Resistance Impedance ()(*1) (mA)(*2) ( max.) (*1) Customer MURATA ESD Rank Values 5A:8kV Part Number Part Number Initial After (at 100MHz) (at 1GHz) at 125 at 150 Values Testing BLM15HG601BH1D 60025 100040 300 20 0.7 0.8 BLM15HG102BH1D 100025 140040 250 20 1.1 1.2 BLM15HD601BH1D 60025% 140040% 300 20 0.85 0.95 5A BLM15HD102BH1D 100025% 200040% 250 20 1.25 1.35 BLM15HD182BH1D 180025% 270040% 200 20 2.00 2.10 Operating Temperature : -55C to +150C Storage Temperature : -55C to +150C (*1) Standard Testing Conditions < Unless otherwise specified > < In case of doubt > Temperature : Ordinary Temp. (15 C to 35 C ) Temperature : 20C2 C Humidity : Ordinary Humidity (25%(RH) to 85%(RH)) Humidity : 60%(RH) to 70%(RH) Atmospheric pressure : 86kPa to 106kPa Rated current at 85C (*2)Rated Current is derated as right figure 125 depending on the operating temperature. Rated current at 121550C 0 85 125 125 150 Operating Temperature (C) 4.Style and Dimensions 1.00.05 0.50.05 Equivalent Circuit 0.250.1 Resistance element becomes () dominant at high frequencies. : Electrode Unit Weight (Typical value) (in mm) 0.001g 5.Marking No marking. MURATA MFG.CO.,LTD. 0.50.05 Rated Current (A)Reference Only Spec.No.JENF243A-9137B-01 P2/8 6.Specifications 6-1.Electrical Performance No. Item Specification Test Method 6-1-1 Impedance Meet item 3. Measuring Frequency : 100MHz1MHz, 1GHz1MHz Measuring Equipment : KEYSIGHT4291A or the equivalent Test Fixture : KEYSIGHT16192A or the equivalent 6-1-2 DC Resistance Meet item 3. Measuring Equipment : Digital multi meter *Except resistance of the Substrate and Wire 6-2.Mechanical Performance (based on Table 13 for FILTER EMI SUPPRESSORS/FILTERS) AEC-Q200 Rev.D issued June. 1 2010 AEC-Q200 Murata Specification / Deviation No. Stress Test Method 3 High 1000hours at 150 deg C Meet Table A after testing. Temperature Set for 24hours Table A Exposure at room temperature, Appearance No damage then measured. Impedance Change Within 40% (at 100MHz) DC Meet item 3. Resistance 4 Temperature Cycling 1000cycles Meet Table B after testing. -55 deg C to +150 deg C TableB Set for 24hours Appearance No damage at room temperature, Impedance then measured. Change Within 50% (at 100MHz) DC Meet item 3. Resistance 5 Destructive Per EIA469 No defects Physical Analysis No electrical tests 7 Biased Humidity 1000hours at 85 deg C, 85%RH Meet Table A after testing. Apply max rated current. 8 Operational Life Apply 150 deg C 1000hours Meet Table A after testing. If the rated current of parts exceed 20 mA, Set for 24hours at the operating temperature should be 125 deg C. room temperature, then measured 9 External Visual Visual inspection No abnormalities 10 Physical Dimension Meet ITEM 4 No defects Style and Dimensions 12 Resistance Per MIL-STD-202 Method 215 Not Applicable to Solvents 13 Mechanical Shock Per MIL-STD-202 Method 213 Meet Table A after testing. Condition F: 1500g s(14.7N)/0.5ms/Half sine 14 Vibration 5g s(0.049N) for 20 minutes,Meet Table A after testing. 12cycles each of 3 oritentations Test from 10-2000Hz. MURATA MFG.CO.,LTD.