BLM18DN601SZ1D Murata

Reference Only Spec.No.JENF243A-9158A-01 P1/8 Chip Ferrite Bead BLM18DNSZ1D Murata Standard Reference Specification AEC-Q200 1.Scope This reference specification applies to Chip Ferrite Bead BLM18DN SZ series for Automotive Electronics based on AEC-Q200 except for Power train and Safety. 2.Part Numbering (ex.) BL M 18 DN 601 S Z 1 D (1) (2) (3) (4) (5) (6) (7) (8) (9) (1)Product ID (4)Characteristics (7)Category(for Automotive Electronics) (2)Type (5)Typical Impedance at 100MHz (8)Numbers of Circuit (3)Dimension (L) (6)Performance (9)Packaging (D:Taping) 3.Rating DC Resistance (*1) Impedance () Rated Current (*1) ( max.) (refer to below comment) (mA) Customer MURATA (refer to below comment) ESD Part Number Part Number Values Rank at at Initial at 100MHz at 1GHz After 85 125 Values Testing BLM18DN151SZ1D 15025% 40030% 1400 900 0.120 0.140 BLM18DN151SZ1B BLM18DN221SZ1D 22025% 65030% 1000 650 0.210 0.255 BLM18DN221SZ1B (*2) 3 BLM18DN381SZ1D 38025% 110030% 850 550 0.325 0.390 BLM18DN381SZ1B BLM18DN601SZ1D 60025% 150030% 700 450 0.435 0.525 BLM18DN601SZ1B Operating Temperature : -55C to +125C Storage Temperature : -55C to +125C (*1) Standard Testing Conditions < Unless otherwise specified > < In case of doubt > Temperature : Ordinary Temp. (15 C to 35 C ) Temperature : 20C2 C Humidity : Ordinary Humidity (25%(RH) to 85%(RH)) Humidity : 60%(RH) to 70%(RH) Atmospheric pressure : 86kPa to 106kPa (*2) Maximum Withstand Voltage 4000 V (DC) to 6000 V (DC) Rated current at 85C (Notes) Rated Current is derated as right figure Rated current at 125C depending on the operating temperature. 0 85 125 4.Style and Dimensions Operating Temperature (C) 1.60.15 0.80.15 Equivalent Circuit Resistance element becomes 0.40.2 () dominant at high frequencies. : Electrode Unit Weight (Typical value) 0.004g (in mm) MURATA MFG.CO.,LTD. 0.80.15 Rated Current (A)Reference Only Spec.No.JENF243A-9158A-01 P2/8 5.Marking No marking. 6.Specifications 6-1.Electrical Performance No. Item Specification Test Method 6-1-1 Impedance Meet item 3. Measuring Frequency : 100MHz1MHz,1GHz1MHz Measuring Equipment : KEYSIGHT 4291A or the equivalent Test Fixture : KEYSIGHT 16192A or the equivalent 6-1-2 DC Resistance Meet item 3. Measuring Equipment : Digital multi meter Except resistance of the Substrate and Wire 6-2.Mechanical Performance (based on Table 13 for FILTER EMI SUPPRESSORS/FILTERS) AEC-Q200 Rev.D issued June. 1 2010 AEC-Q200 Murata Specification / Deviation No.Stress Test Method 3 High 1000hours at 125 deg C Meet Table A after testing. Temperature Set for 24hours Table A Appearance No damage Exposure at room temperature, Impedance Change then measured. Within 50% (at 100MHz) DC Resistance Meet item 3. 4 Temperature Cycling 1000cycles Meet Table B after testing. -55 deg C to +125 deg C Table B Appearance No damage Set for 24hours Impedance Change Within 30% at room temperature, (at 100MHz) then measured. DC Resistance Meet item 3. 5 Destructive Per EIA469 No defects Physical Analysis No electrical tests 7 Biased Humidity 1000hours at 85 deg C, 85%RH Meet Table A after testing. Apply max rated current. Meet Table A after testing. 8 Operational Life Apply 125 deg C 1000hours Set for 24hours at room temperature, then measured 9 External Visual Visual inspection No abnormalities 10 Physical Dimension Meet ITEM 4 No defects Style and Dimensions 12 Resistance Per MIL-STD-202 Method 215 Not Applicable to Solvents 13 Mechanical Shock Per MIL-STD-202 Method 213 Meet Table B after testing. Condition F: 1500g s(14.7N)/0.5ms/Half sine 14 Vibration 5g s(0.049N) for 20 minutes,Meet Table B after testing. 12cycles each of 3 oritentations Test from 10-2000Hz. 15 Resistance Solder temperature Pre-heating: 150C +/-10 deg C, 60s to 90s to Soldering Heat 260C+/-5 deg C Immersion time 10s Meet Table A after testing. 17 ESD Per AEC-Q200-002 ESD Rank: Meet Item 3 (Rating) Meet Table A after testing. 18 Solderability Per J-STD-002 Method b : Not Applicable 95% of the terminations is to be soldered. 19 Electrical Measured : Impedance No defects Characterization MURATA MFG.CO.,LTD.