BLM41PG102SZ1L Murata

Spec. No. JENF243A-9116C-01 R e fe re nce Onl y P.1/9 Chip Ferrite Bead BLM41SZ1L Murata Reference Specification AEC-Q200 1. Scope This reference specification applies to Chip Ferrite Bead for Automotive Electronics BLM41 SZ Series based on AEC-Q200 except for Power train and Safety. 2. Part Numbering (ex.) BL M 41 PG 600 S Z 1 L (1) (2) (3) (4) (5) (6) (7) (8) (9) (1)Product ID (4)Characteristics (7)Category (for Automotive Electronics) (2)Type (5)Typical Impedance at 100MHz (8)Numbers of Circuit (3)Dimension (L) (6)Performance (9)Packaging (L: Taping) 3. Rating Impedance () DC Resistance Rated Current (at 100MHz,Under Standard () max. (mA) (*1) Customer MURATA ESD Rank Testing Condition) Initial Values Part Number Part Number 2:2kV Values After at at Typical Testing 85 125 *1 *1 BLM41PG600SZ1L 30 min. 60 0.009 0.018 6000 3700 *1 *1 BLM41PG750SZ1L 45 min. 75 0.015 0.03 3500 2450 *1 *1 BLM41PG181SZ1L 18025 180 0.02 0.04 2 3500 2100 *1 *1 BLM41PG471SZ1L 47025% 470 0.05 0.10 2000 1350 *1 *1 BLM41PG102SZ1L 100025% 1000 0.09 0.18 1500 1000 Operating Temperature: -55C to +125C Storage Temperature: -55C to +125C (*1) Standard Testing Conditions < Unless otherwise specified > < In case of doubt > Temperature : Ordinary Temp. (15 C to 35 C ) Temperature : 20C2 C Humidity : Ordinary Humidity (25%(RH) to 85%(RH)) Humidity : 60%(RH) to 70%(RH) Atmospheric pressure : 86kPa to 106kPa 85 x Describe the Rated current as x A (*2) In case of Rated current is more than *1, in case of more than 1A. Rated Current is derated as right figure 1251 depending on the operating temperature. 0 85 125 Operating Temperature (C) 4. Style and Dimensions 4.50.2 1.60.2 Equivalent Circuit 0.70.3 Resistance element becomes () dominant at high frequencies. : Electrode Unit Mass (Typical value) 0.050g (in mm) MURATA MFG.CO., LTD. 1.60.2 Rated Current (A)Spec. No. JENF243A-9116C-01 R e fe re nce Onl y P.2/9 5. Marking No marking. 6. Specifications 6-1. Electrical Performance No. Specification Test Method Impedance Meet item 3. Measuring Frequency : 100MHz1MHz 7-1-1 Measuring Equipment : Agilent 4291A or the equivalent Test Fixture : Agilent 16192A or the equivalent 7-1-2 DC Resistance Meet item 3. Measuring Equipment : Digital multi meter 6-2. Mechanical Performance (based on Table 13 for FILTER EMI SUPPRESSORS/FILTERS) AEC-Q200 Rev.D issued June 1. 2010 AEC-Q200 Murata Specification / Deviation No. Stress Test Method 3 High 1000hours at 125 deg C Meet Table A after testing. Temperature Set for 24hours at room Table A Exposure temperature, then measured. Appearance No damage Impedance Change Within 30% (at 100MHz) DC Meet item 3. Resistance 4 Temperature Cycling 1000cycles Meet Table A after testing. -55 deg C to +125 deg C Set for 24hours at room temperature, then measured. 5 Destructive Per EIA469 No defects Physical Analysis No electrical tests 7 Biased Humidity 1000hours at 85 deg C, Meet Table A after testing. 85%RH Apply max rated current. Meet Table A after testing. 8 Operational Life Apply 125 deg C 1000hours If the rated current of parts exceed 1A, Set for 24hours at room the operating temperature should be 85 deg C. temperature, then measured External Visual Visual inspection No abnormalities 9 10 Physical Dimension Meet ITEM 4 No defects Style and Dimensions 12 Resistance to Solvents Per MIL-STD-202 No defects Method 215 13 Mechanical Shock Per MIL-STD-202 Method 213 Meet Table A after testing. 1500g s(14.7N)/0.5ms/ Half sine 14 Vibration 5g s (0.049N) for 20 minutes, Meet Table A after testing. 12cycles each of 3 orientations Test from 10-2000Hz. 12cycles each of 3 orientations MURATA MFG.CO., LTD.