MLSC Design Chip Multilayer Ceramic Capacitors for Automotive GCD21BR72A393KA01 (0805, X7R:EIA, 39000pF, DC100V) : packaging code Reference Sheet 1.Scope This product specification is applied to MLSC Design Chip Multilayer Ceramic Capacitors used for Automotive Electronic equipment. 2.MURATA Part NO. System (Ex.) GCD 21 B R7 2A 393 K A01 L (1)L/W (2)T (3)Temperature (4)Rated (5)Nominal (6)Capacitance (7)Muratas Control (8)Packaging Code Dimensions Dimensions Characteristics Voltage Capacitance Tolerance Code 3. Type & Dimensions (Unit:mm) (1)-1 L (1)-2 W (2) T e g 2.00.15 1.250.15 1.250.15 0.2 to 0.7 0.7 min. 4.Rated value (3) Temperature Characteristics Specifications and Test (4) (6) (Public STD Code):X7R(EIA) (5) Nominal Methods Rated Capacitance Temp. coeff Temp. Range Capacitance (Operating Voltage Tolerance Temp. Range) orCap. Change (Ref.Temp.) -55 to 125 C -15 to 15 % DC 100 V 39000 pF 10 % -55 to 125 C (25 C) 5.Package mark (8) Packaging Packaging Unit f180mm Reel L 3000 pcs./Reel EMBOSSED W8P4 f330mm Reel K 10000 pcs./Reel EMBOSSED W8P4 Product specifications in this catalog are as of Apr.25,2018,and are subject to change or obsolescence without notice. Please consult the approval sheet before ordering. Please read rating and Cautions first. GCD21BR72A393KA01-01 1AEC-Q200 Murata Standard Specification and Test Methods No AEC-Q200 Test Item Specification. AEC-Q200 Test Method Pre-and Post-Stress 1 - Electrical Test 2 High Temperature The measured and observed characteristics should satisfy Solder the capacitor on the test substrate(glass epoxy board). Exposure (Storage) the specifications in the following table. Set the capacitor for 1000+/-12h at 150+/-3. Appearance No marking defects Set for 24+/-2h at room temperature, then measure. Initial measurement Capacitance Within +/-10.0% Perform a heat treatment at 150+0/-10 for 1h and then sit Change for 24+/-2h at room temperature.Perform the initial measurement. D.F. 0.03 max. I.R. Within the specified initial value. 25 3 Temperature Cycling The measured and observed characteristics should satisfy Solder the capacitor on the test substrate(glass epoxy board). the specifications in the following table. Perform the 1000 cycles test according to the four heat treatments Appearance No marking defects listed in the following table. Set for 24+/-2h at room temperature, then measure. Step 1 2 3 4 Capacitance Within +/-10.0% Temp. Room Room Min.Operating Temp.+0/-3 Max.Operating Temp. +3/-0 ( C) Temp. Temp. Change Time 15+/-3 1 15+/-3 1 (min) D.F. 0.03 max. Initial measurement Perform a heat treatment at 150+0/-10 for 1h and then sit I.R. Within the specified initial value. for 24+/-2h at room temperature.Perform the initial measurement. 25 4 Destructive No defects or abnormalities Per EIA-469. Physical Analysis 5 Moisture Resistance The measured and observed characteristics should satisfy Solder the capacitor on the test substrate(glass epoxy board). Apply the 24h heat (25 to 65) and humidity (80%RH to 98%RH) the specifications in the following table. treatment shown below, 10 consecutive times. Appearance No marking defects Set for 24+/-2h at room temperature, then measure. Humidity Humidity Temperature 80 98% 8098% Capacitance Within +/-12.5% Humidity Humidity Humidity () 9098% 9098% 9098% 70 Change 65 60 55 D.F. 0.03 max. 50 45 40 35 30 I.R. Within the specified initial value. 25 20 +10 25 - 2 15 10 5 Initial measuremt 0 -5 -10 One cycle 24hours 0 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 Hours Initial measurement Perform a heat treatment at 150+0/-10 for 1h and then sit for 24+/-2h at room temperature.Perform the initial measurement. 6 The measured and observed characteristics should satisfy Biased Humidity Solder the capacitor on the test substrate(glass epoxy board). the specifications in the following table. Apply the rated voltage and 1.3+0.2/-0Vdc (add 6.8k resister) at 85+/-3 and 80%RH to 85%RH humidity for 1000+/-12h. Appearance No marking defects The charge/discharge current is less than 50mA. Remove and set for 24+/-2h at room temperature, then measure. Capacitance Within +/-12.5% Change Initial measurement D.F. 0.035 max. Perform a heat treatment at 150+0/-10 for 1h and then sit for 24+/-2h at room temperature.Perform the initial measurement. I.R. More than 1,000M or 50F 25 (Whichever is smaller) JEMCGS-02081C 2