NFZ03SG501SN10D Murata

Reference Only Spec.No.JENF243J-0016D-01 P1/7 CHIP NOISE FILTER NFZ03SGSN10 REFERENCE SPECIFICATION 1.Scope This reference specification applies to Chip Noise Filter NFZ03SG Series. 2.Part Numbering (ex) NF Z 03 SG 331 S N 1 0 D Product ID Structure Dimension Characteristics Typical Impedance Performance Category Numbers special Packaging (LW) at 900MHz of speci- D:Taping Circuit fication * B: BULK 0High Impedance 3.Rating Impedance () (Under Standard DC Resistance Rated Customer MURATA Testing Condition) () Current Part Number Part Number at 900MHz at 1.7GHz (mA) Typ. Min. Typ. Typ. Max. NFZ03SG331SN10D 330 200 400 0.46 0.55 305 NFZ03SG331SN10B NFZ03SG501SN10D 500 300 600 0.56 0.68 275 NFZ03SG501SN10B NFZ03SG671SN10D 670 400 800 0.69 0.85 250 NFZ03SG671SN10B NFZ03SG102SN10D 1000 600 900 1.00 1.20 210 NFZ03SG102SN10B NFZ03SG162SN10D 1600 960 1200 1.30 1.60 180 NFZ03SG162SN10B Operating Temperature : -55C to +125C Storage Temperature : -55C to +125C 4.Style and Dimensions 0.30.03 0.60.03 Equivalent Circuit 0.150.05 Resistance element becomes () dominant at high frequencies. :Electrode Unit Mass(Typical value) (in mm) 0.300mg 5.Marking No marking. 6.Standard Testing Conditions < Unless otherwise specified > < In case of doubt > Temperature : Ordinary Temp. (15 C to 35 C ) Temperature : 20C2 C Humidity : Ordinary Humidity (25%(RH) to 85%(RH)) Humidity : 60%(RH) to 70%(RH) Atmospheric pressure : 86kPa to 106kPa 7.Specifications 7-1.Electrical Performance No. Item Specification Test Method 7-1-1 Impedance Meet item 3. Measuring Frequency : 900MHz, 1.7GHz1MHz Measuring Equipment : KEYSIGHT 4991A or the equivalent Test Fixture : KEYSIGHT 16192A /16197Aor their equivalents 7-1-2 DC Resistance Measuring Equipment : Digital multi meter *Except resistance of the Substrate and Wire MURATA MFG.CO.,LTD. 0.30.03Reference Only Spec.No.JENF243J-0016D-01 P2/7 7-2.Mechanical Performance No. Item Specification Test Method 7-2-1 Bonding Products shall not be damaged It shall be soldered on the substrate. Strength after tested as test method. Applying Force(F) : 2N Applying Time : 5s 7-2-2 Bending It shall be soldered on the Glass-epoxy substrate. Strenght Substrate : 100mm40mm0.8mm Deflection : 2.0mm Speed of Applying Force : 1.0mm/s Keeping Time : 20s Pressure jig F R230 Deflection (in mm) Product 45 45 7-2-3 Vibration Appearance: No damage It shall be soldered on the substrate. Oscillation Frequency : 10Hz to 2000Hz to 10Hz for 20min Total amplitude 3.0mm or Acceleration 2 amplitude 196 m / s whichever is smaller. Testing Time:A period of 2h in each of 3 mutually perpendicular directions.(Total 6h) 7-2-4 Solderability The electrodes shall be at Flux : Ethanol solution of rosin,25(wt)% least 95% covered with new Pre-Heating : 150C, 60s solder coating. Solder : Sn-3.0Ag-0.5Cu Solder Temperature : 245C3C Immersion Time : 3s 7-3.Environmental Performance It shall be soldered on the substrate. No. Item Specification Test Method 7-3-1 Heat Life Meet Table 1. Temperature : 125C2C Table 1 Applying Current : Rated Current Time : 1000h(+48h,-0h) Appearance No damage Then measured after exposure in the room Impedance condition for 4 to 48 h. Change Within 30% 7-3-2 Cold (at 900MHz) Temperature : -55C2C Resistance Time : 1000h(+48h,-0h) Then measured after exposure in the room condition for 4 to 48 h. 7-3-3 Humidity Temperature : 40C2C Humidity : 90%(RH) to 95%(RH) Time : 1000h(+48h,-0h) Then measured after exposure in the room condition for 4 to 48 h. 7-3-4 Temperature 1 cycle : Cycle 1 step : -55 C(+0 C,-3 C) /30min(+3min,-0min) 2 step : Ordinary temp. / 3 min max. 3 step : +125 C(+3 C,-0 C) / 30min(+3min,-0min) 4 step : Ordinary temp. / 3 min max. Total of 100 cycles Then measured after exposure in the room condition for 4 to 48 h. MURATA MFG.CO.,LTD.