CL03C220GA3GNNH Samsung

(Reference sheet) SPECIFICATION Supplier : Samsung electro-mechanics Samsung P/N : CL03C220GA3GNNH Product : Multi-layer Ceramic Capacitor Description : CAP, 22, 25V, 2%, C0G, 0201 A. Samsung Part Number 03 C 220 G A 3 G N N H CL Series Samsung Multi-layer Ceramic Capacitor Size 0201 (inch code) L: 0.60 0.03 mm W: 0.30 0.03 mm Dielectric C0G Inner electrode Cu Capacitance 22 Termination Cu Capacitance 2 Plating Sn 100% (Pb Free) % tolerance Product Normal Rated Voltage 25 V Special Reserved for future use Thickness 0.30 0.03 mm Packaging Cardboard Type, 7 reel B. Samsung Reliability Test and Judgement condition Performance Test condition Capacitance Within specified tolerance 0.5~5Vrms 110% Q 840 min Insulation Rated Voltage 60~120 sec. 10,000Mohm or 500Mohm Resistance Whichever is Smaller Appearance No abnormal exterior appearance Microscope ( 10) Withstanding No dielectric breakdown or 300% of the rated voltage Voltage mechanical breakdown Temperature C0G characteristics (From -55 to 125, Capacitance change should be within 30PPM/) Adhesive Strength No peeling shall be occur on the 200gF, for 101 sec. of Termination terminal electrode Bending Strength Capacitance change : Bending to the limit (1mm) with 1.0mm/sec. within 5% or 0.5 whichever is larger Solderability More than 75% of terminal surface SnAg3.0Cu0.5 solder is to be soldered newly 2455, 30.3sec. (preheating : 80~120 for 10~30sec.) Resistance to Capacitance change : Solder pot : 2705, 101sec. Soldering heat within 2.5% or 0.25 whichever is larger Tan , IR : initial spec.Performance Test condition Vibration Test Capacitance change : Amplitude : 1.5mm within 2.5% or 0.25 whichever is larger From 10 to 55 (return : 1min.) Tan , IR : initial spec. 2hours 3 direction (x, y, z) Moisture Capacitance change : With rated voltage Resistance within 7.5% or 0.75 whichever is larger 402, 90~95%RH, 500+12/-0hrs Q : 173.33 min IR : 500Mohm or 25Mohm Whichever is Smaller High Temperature Capacitance change : With 200% of the rated voltage Resistance Max. operating temperature within 3% or 0.3 whichever is larger Q : 330 min 1000+48/-0hrs IR : 1000Mohm or 50Mohm Whichever is Smaller Temperature Capacitance change : 1 cycle condition Cycling Min. operating temperature within 2.5% or 0.25 whichever is larger 25 Tan , IR : initial spec. Max. operating temperature 25 5 cycle test C. Recommended Soldering method : Reflow ( Reflow Peak Temperature : 260+0/-5, 10sec. Max ) PProdductt specififiicatitions iinclluddedd iin tthhe speciiffiicatitions are effffectitive as off MMarchh 11, 20132013. Please be advised that they are standard product specifications for reference only. We may change, modify or discontinue the product specifications without notice at any time. So, you need to approve the product specifications before placing an order. Should you have any question regarding the product specifications, please contact our sales personnel or application engineers.