VJ0805H392KXABC31X Vishay

VJ....31X RoHS Automotive MLCC www.vishay.com Vishay Vitramon Surface Mount Multilayer Ceramic Chip Capacitors for Automotive Applications FEATURES AEC-Q200 qualified with PPAP available Available in 0402 to 1812 body size High operating temperature Wet build process Reliable Noble Metal Electrode (NME) system Parts compliant with ELV directive Material categorization: for definitions of compliance please see www.vishay.com/doc 99912 For more than 25 years Vishay Vitramon has supported the automotive industry with robust, highly reliable MLCCs that have made it a leader in this segment. All Vishay Vitramon MLCCs are manufactured in Precious Metal Technology (PMT / NME) and a wet build process. They are qualified according to AEC-Q200 with PPAP available on request. Applications for these devices include automotive under the hood, safety and comfort electronics. Their termination finish is 100 % matte tin plate finish. A polymer (flexible) termination with 100 % matte tin plate finish is offered for boardflex sensitive applications. C0G (NP0) DIELECTRIC X7R, X8R DIELECTRIC GENERAL SPECIFICATION GENERAL SPECIFICATION Note Note Electrical characteristics at +25 C unless otherwise specified Electrical characteristics at +25 C unless otherwise specified Operating Temperature: -55 C to +150 C Operating Temperature: -55 C to +150 C (above +125 C changed characteristics, see 2.2) (X7R above +125 C changed characteristics, see 2.2) Capacitance Range: 1 pF to 22 nF Capacitance Range: 120 pF to 1.0 F Voltage Range: 25 V to 3000 V Voltage Range: 16 V to 1000 V DC DC DC DC Temperature Coefficient of Capacitance (TCC): Temperature Coefficient of Capacitance (TCC): 0 ppm/C 30 ppm/C from -55 C to +125 C X7R: 15 % from -55 C to +125 C, with 0 V applied DC X8R: 15 % from -55 C to +150 C, with 0 V applied DC Dissipation Factor (DF): 0.1 % maximum at 1.0 V and Dissipation Factor (DF): RMS 1 MHz for values 1000 pF 16 V, 25 V ratings: 3.5 % maximum at 1.0 V and 1 kHz RMS 0.1 % maximum at 1.0 V and > 25 V ratings: 2.5 % maximum at 1.0 V and 1 kHz RMS RMS 1 kHz for values > 1000 pF Insulating Resistance: Insulating Resistance: at +25 C 100 000 M min. or 1000 F whichever is less at +25 C 100 000 M min. or 1000 F whichever is less at +125 C 10 000 M min. or 100 F whichever is less at +125 C 10 000 M min. or 100 F whichever is less Aging Rate: 1 % maximum per decade Aging: 0 % maximum per decade Dielectric Strength Test: Dielectric Strength Test: performed per method 103 of EIA 198-2-E. performed per method 103 of EIA 198-2-E. Applied test voltages Applied test voltages 250 V -rated: 250 % of rated voltage DC 250 V -rated: 250 % of rated voltage 500 V -rated: min. 150 % of rated voltage DC DC 500 V -rated: 200 % of rated voltage 630 V , 1000 V -rated: min. 120 % of rated voltage DC DC DC 630 V , 1000 V -rated: 150 % of rated voltage DC DC 3000 V -rated: 120 % of rated voltage DC Revision: 06-Nov-14 Document Number: 45226 1 For technical questions, contact: mlcc vishay.com THIS DOCUMENT IS SUBJECT TO CHANGE WITHOUT NOTICE. THE PRODUCTS DESCRIBED HEREIN AND THIS DOCUMENT ARE SUBJECT TO SPECIFIC DISCLAIMERS, SET FORTH AT www.vishay.com/doc 91000 VJ....31X RoHS Automotive MLCC www.vishay.com Vishay Vitramon QUICK REFERENCE DATA CAPACITANCE MAXIMUM VOLTAGE DIELECTRIC CASE CODE (V) MINIMUM MAXIMUM 0402 100 1.0 pF 220 pF 0603 200 1.0 pF 1.0 nF 0805 500 1.0 pF 3.9 nF C0G (NP0) 1206 630 1.0 pF 10 nF 1210 630 100 pF 12 nF 1812 3000 12 pF 22 nF 0402 100 120 pF 47 nF 0603 200 330 pF 150 nF 0805 250 330 pF 470 nF X7R 1206 1000 220 pF 1.0 F 1210 630 390 pF 1.0 F 1812 630 10 nF 1.0 F 0402 100 330 pF 6.8 nF 0603 100 470 pF 33 nF X8R 0805 100 470 pF 100 nF 1206 50 1.0 nF 220 nF 1210 50 10 nF 220 nF Note Detail ratings see Selection Chart Revision: 06-Nov-14 Document Number: 45226 2 For technical questions, contact: mlcc vishay.com THIS DOCUMENT IS SUBJECT TO CHANGE WITHOUT NOTICE. THE PRODUCTS DESCRIBED HEREIN AND THIS DOCUMENT ARE SUBJECT TO SPECIFIC DISCLAIMERS, SET FORTH AT www.vishay.com/doc 91000